Electronics Forum: leadfree and bga and lead and process (Page 1 of 6)

Wave solder pallets: lead and lead-free process

Electronics Forum | Wed Jul 27 15:54:44 EDT 2005 | Hiram

Hi everybody, We have wave solder fixtures made of Durapol and multiple wave solder machines. Most likely we�ll use the same pallets for either tin-lead or lead-free solder for a while (of course after washing the pallets). Should we test the palle

Wave solder pallets: lead and lead-free process

Electronics Forum | Wed Jul 27 16:27:57 EDT 2005 | GS

It may be you should look for higher TG of Durapol Rgds GS

Wave solder pallets: lead and lead-free process

Electronics Forum | Wed Jul 27 22:09:49 EDT 2005 | Ken

My policy is not to mix them. You have zero cross contamination potiental with this policy.

Wave solder pallets: lead and lead-free process

Electronics Forum | Wed Jul 27 16:46:48 EDT 2005 | russ

I don't think that you would need to test these. Have you ever seen any evidence of solder sticking to them? We use the same material and never notice anything besides flux staying on the bottom. Would the lead absorption if any even be of a concer

lead free platings and tin lead

Electronics Forum | Tue Aug 31 17:36:36 EDT 2004 | davef

NO-LEAD COMPONENTS WITH LEAD SOLDER ISSUE: We agree with Russ. We've dicussed this several times on SMTnet. For instance, look here http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=25394 LEAD COMPONENTS WITH NO-LEAD SOLDER ISSUE: We disa

Time and temp in lead and lead-free reflow

Electronics Forum | Sat Aug 02 08:06:11 EDT 2008 | pcbbuilders

Is there a limit to the time that most components can stay at temperatures around 130-200 deg c? if i slow the time, the first 4 zones will be at this temp for about 5 minutes in no lead process. i am concerned that some chips wont be rated at this t

Time and temp in lead and lead-free reflow

Electronics Forum | Mon Aug 04 09:30:16 EDT 2008 | grics

If you have concerns, you can look at the datasheet for each component or contact one of their application or materials engineers and find out what the components are rated for...process-wise. IE, how long can I be in the oven with this part, at what

PB-Free HASL and Leaded Solder

Electronics Forum | Thu May 13 20:40:25 EDT 2021 | winston_one

Yes, we can't use pure Pb PROCESS. And as I say we will not use it anyway, as we have lead-free BGA's, LGAs, component with Solder Charged Terminations... It's became almost normal practice to solder it with leaded solder pastes. In this case peak re

Can lead free and non lead free production mix in the same mach

Electronics Forum | Wed Apr 26 07:37:34 EDT 2006 | amol_kane

"Can we reuse the same machine? My point here is that the non lead free process has already coated the machine interior ( exhaust, internal flow ) with leaded component, and by conversion to lead free are we containminating the lead free product from

Can lead free and non lead free production mix in the same mach

Electronics Forum | Wed Apr 26 07:37:52 EDT 2006 | amol_kane

"Can we reuse the same machine? My point here is that the non lead free process has already coated the machine interior ( exhaust, internal flow ) with leaded component, and by conversion to lead free are we containminating the lead free product from

  1 2 3 4 5 6 Next

leadfree and bga and lead and process searches for Companies, Equipment, Machines, Suppliers & Information

Cleaning Machine For Electronic Assembly

MSD Dry Cabinets
Sell Your Used SMT & Test Equipment

Easily dispense fine pitch components with ±25µm positioning accuracy.
FPC* - Fluid Pressure Control - Dispensing Pump

High Throughput Reflow Oven
Assembly Automation Technology

MIRTEC - the Global Leader in PCB INSPECTION Technology.