Electronics Forum: lifted pads peel strength (Page 1 of 3)

Solder joint strength

Electronics Forum | Tue Mar 22 07:39:05 EST 2005 | davef

There is no standard. This is a relative test. If you wish to do tests of this kind, we suggest to pay attention to the following points: * Shear strength of soft solder depends on the deformation speed applied. The faster the material is deformed t

Re: Shear strength and Copper/Tin Intermetalic layer

Electronics Forum | Thu Jul 09 21:04:50 EDT 1998 | Dave F

| Hi there, | I am looking for some informations concerning the shear or pull strength of a typical TQFP 20 mils leads in relationship with the Copper/Tin intermetalic layer thickness. Could anyone help? | | Thank in advandce. | rgs, | chiakl Chiakl

Bare PCB baking

Electronics Forum | Fri Nov 22 08:57:56 EST 2002 | davef

Q1: What do you mean by "if the board is manufactured properly"? A2: If the epoxy is noy cured prooperly, for instance, the copper will not be well attached to the glass. So, peel strength will be lower. Q2: I don't believe that the peel off/or lif

Bare PCB baking

Electronics Forum | Wed Nov 20 21:04:15 EST 2002 | yngwie

Hi Dave, What do you mean by "if the board is manufactured properly". If the board is not manufactured properly, humidity will have an impact on the peel strength? Is that what you mean. How does the Humidity impacted the peel strength ? Thru' which

Bare PCB baking

Electronics Forum | Wed Nov 20 16:53:18 EST 2002 | davef

Q1: How important is the bare PCB baking ? A1: Baking boards is a non-value added activity. Q2: What is the temperature for baking @ what RH ? A2: Search the fine SMTnet Arcives for bake recipes. Q3: What would be the impact for the ENTEK finishe

Component Peel Strenght

Electronics Forum | Tue Oct 10 13:32:26 EDT 2006 | rsteele

Does anyone know of any tests or testing done on the peel strength of components to pads. I have alot of info on FAB level peel strength testing, but nothing on components themselves. Is there any process(es) to test and insure new pastes and reflo

Re: copper land delamination

Electronics Forum | Mon Nov 15 21:35:50 EST 1999 | Dave F

Bob Bob: Fortunately, you found this before you built-up a lot of product. Some thoughs and other drivel: 1 Use IPC-TM-650, Method 2.4.8 for copper peel with a Instron machine. Typical pad peel strength requirement for FR-4, 2 oz. copper is: 6 l

Re: Passive component shear Testing

Electronics Forum | Tue May 23 20:39:37 EDT 2000 | Dave F

Scott: Sounds like fun: � Solder joint strength in pull/shear varies with lead geometry, solder volume, lead metal/metallization, and the test method. � Among things, IPC-TM-650 talks to getting pads off-of boards. For instance: Method 2.4.8 is for

Battery Nickel strips soldering in HASL PCB finish

Electronics Forum | Mon Nov 26 13:40:40 EST 2018 | robl

Hi Prem, Yes, the flux in the Cobar paste helped with wetting and joint strength, as does reducing voids as there is more solder in the joint, as does cooling rate. Regarding peel test in KG, it depends on the pad size and volume of solder in the j

force between the pad and laminate material

Electronics Forum | Wed Jun 12 08:13:29 EDT 2002 | davef

Don't sound proper. There is no specification. Pad peel strength test methods are: * IPC-TM-650, Method 2.4.21 for multiple solderings * IPC-TM-650, Method 2.4.8 for copper peel with a Instron machine. Typical requirement for Cu is: 6 lbf/in [1

  1 2 3 Next