Electronics Forum | Mon Feb 10 09:49:32 EST 2003 | pjc
For manual X-ray systems: Kv power to start off with. Depending on what type of components you have to X-ray, you may be ok w/ just a 90Kv system, for example. Its not all about Kv though. With most systems you can adjust to quantity of X-rays you ar
Electronics Forum | Mon Feb 10 21:19:51 EST 2003 | MA/NY DDave
Hi I am in favor of the best money can buy tiles, and everything including an ESD officier and training for everyone. Long term less money is spent and ESD protection is kept high continually. Boy do I have stories like the cleaning guys who put on
Electronics Forum | Thu Mar 27 22:00:27 EST 2003 | davef
Enrique It's true that higher energy guns do a better job measuring "light" materials. [Actually, if that was true by itself, you'd expect the fabricator's readings to be higher than yours. But, HEY!!!] Regardless, there's alot more to getting an
Electronics Forum | Tue Mar 11 18:01:26 EST 2003 | russ
Tim, I cannot remember what model our T.D. wave was it was a small unit about 8 ft. long "tabletop" is what I call them. In keeping up with this thread I noticed a lot of T.D. support. So, I decided to backtrack and review history with my previous pe
Electronics Forum | Thu Feb 27 11:05:49 EST 2003 | Chris
Hello, I am the manager of a Drafting department and don�t pretend to know too much about the SMT process. But I am the manager of a CAD designer so I am somewhat responsible for the following issue. So since no one else around here seems to have the
Electronics Forum | Fri Mar 07 12:27:04 EST 2003 | msivigny
Hello Doug, thank you for the additional commentary, it has reminded me of another reflow recommendation that I'd like to make in general for readers. It's not specific to O2/N2 in ovens but in the method for creating and managing profiles for numero
Electronics Forum | Wed Mar 05 22:35:40 EST 2003 | MA/NY DDave
Hi Just a few notes below on this forum the same thing was discussed. It probably would have been better to update that note rather than start a new tread. Hey it makes it easier for all or us and YOU. Check the note out, and also check the archive
Electronics Forum | Sat Mar 08 02:23:09 EST 2003 | Frank
My two Process Engineers are at odds with each other. One says that the Tact Time is only the actual Pick-n-Place time to build a board, and the other says it needs to include the load/unload time as well as the Fiducial reading time. Example: So
Electronics Forum | Tue Apr 01 09:58:52 EST 2003 | davef
You're entirely correct. The gold is most likely gone away. [Don't forget you can check if the surface is still solderable with a hand soldering iron.] We're not sure it it will give you the results you seek, but consider using a dye penetrant fai
Electronics Forum | Tue Apr 01 11:50:08 EST 2003 | rdr
Dave, thanks for the info. This sounds like it would verify the presence of an open. We have verified that these balls are open and I am trying to figure out if we are fracturing or not wetting. causing these opens. I would use the die method on ne