Electronics Forum | Wed Aug 10 20:30:49 EDT 2005 | slthomas
I've got a new board (actually a new panel...a 4 up, with one row rotated, where it was a 2 up panel with no rotation before) that runs fine on the IVc but not on the IIIc. I've used the same reference points for the image rotation (fiducials) on bot
Electronics Forum | Fri Sep 02 05:10:21 EDT 2005 | pyramus
Hi I just would like to ask some assistance how to convert a line using a leaded process to a lead-free process? Is there a need for us to change any equipment? printer/reflow? Currently, we are not yet in full 100% lead-free process yet so most lik
Electronics Forum | Tue Oct 18 12:38:19 EDT 2005 | killer1994
Heller, by far the best oven we have had, It has never been down and we've had it over 10 years now. The other two ovens we have are Quad and they are by far the worst piece of garbage ever put out on the market. Broken every other day. We have looke
Electronics Forum | Sun Oct 30 00:54:07 EDT 2005 | Mika
Hello mr. vickt. I do not buy your sales argument, despite it sounds like a good bargain for UIC. The truth is that every new machine/option newer worked from the beginning (this goes for every vendor/manufactory). The costs for dealing with the "so
Electronics Forum | Wed Nov 09 12:06:33 EST 2005 | Rob
I don't want to throw a spanner in the works here, but a large proportion of chip resistors & capacitors have been ROHS compliant for a couple of years now, the manufacturers have just not declaired it. Could it be that the part you have just has
Electronics Forum | Thu Dec 15 02:09:22 EST 2005 | tk380514
SNAGGLETOOTH HOLDS HIS HANDS UP, HAVING JUST REACHED THE EDGE OF HIS OWN IGNORNACE. I just read up on black pads - http://www.emsnow.com/npps/story.cfm?ID=9784 when i checked the joints under the microscope they were a light grey slightly discolou
Electronics Forum | Thu Dec 15 08:09:06 EST 2005 | GS
Hi Liza, several years ago we had problem like that only with Carrier Tape made by Ploycarbonate material and by using High Speed pick & place. Very few pbms met by using low speed P&P machine. Problems have been solved by using Polystirene Carri
Electronics Forum | Wed Dec 21 12:12:44 EST 2005 | mmjm_1099
Hello all, I am a contract manufacturer and I got handed the project of looking up our parts and seeing what's lead-free and what's not. Well my question would be how is your purchasing dept handling this. I would like some input on this from alot of
Electronics Forum | Fri Apr 28 21:20:43 EDT 2006 | Baer
So what is your company? P. KAY is not aware of you or of this situation and we would like to discuss it. The only way that you could have what you claim is if the maintenance were not done and if spent MS2 were left on the solder pot for days. Like
Electronics Forum | Thu Jan 12 02:08:47 EST 2006 | adeline_ko
Hi, What is the different between Electroless Nickel / Immersion Gold (ENIG) and Immersion Au. Are they refer to the same finishing? We has been using the Gold thickness (0.00005 - 0.00013mm) , nicket (0.0025mm) for all Gold finishing brd (Immersio