Electronics Forum | Mon Jul 26 14:14:13 EDT 1999 | Dave F
| | Despite the goodness of Dave F. and George Verboven, I was unable to find the damned single pin connector. As a last attempt, I've draw it (see the link) | | If somebody knows where can buy it, please help me | | (and sorry for to ruin the Eng
Electronics Forum | Fri Jul 16 13:33:31 EDT 1999 | Dale
We are converting from COB to SMT on a product line and want to optomize the PCB as far as Laminate, plating, passivation etc. This is a high temp application 150C. We are presently using BT Laminate but would like to get away from this. We are lo
Electronics Forum | Sat Jul 17 03:02:58 EDT 1999 | Jeff Sanchez
| | | | | I need a good chemical to remove the lacquer finish off of magnet wire. I know there are different kinds but I need one that really works. Any suggestions would be great. thanks in advance guys. | | | | | | | | | What is it you're trying t
Electronics Forum | Mon Jul 12 08:34:26 EDT 1999 | M Cox
| | I am looking for suppliers of ESD floor coverings. I currently have ESD carpet and I would like to replace them with ESD Tile. Help Me | | | | MD Cox | | | | Try a search in the archives. A while back someone asked for similar information.
Electronics Forum | Fri Jul 09 17:50:20 EDT 1999 | Jim Blankenhorn
Hi Carol- What you are asking for can be done. Variables you must account for include the paste viscosity, dispensing head speed, dispenser height relative to board surface, and needle size. You can use most any semi-automated system such as Camalo
Electronics Forum | Sat Jul 10 01:45:45 EDT 1999 | Scott
| Do you have experience with reflow process of a straddle mount connector on a 1.6 mm PCB ? | Connector have more than 200 pins | | What is the process ? | | Thanks | Depends on the connector... For connectors that have pre-applied solder such as
Electronics Forum | Fri Jul 02 09:54:02 EDT 1999 | John Thorup
| | | | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design)
Electronics Forum | Fri Jul 02 10:06:17 EDT 1999 | John Thorup
| | | | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design)
Electronics Forum | Fri Jun 25 01:11:31 EDT 1999 | Vinesh Gandhi
| | | Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody
Electronics Forum | Tue Jun 22 15:42:26 EDT 1999 | Dave F
| | exactly how do you access posted library articles? | | Are you refering to the newest posting by Chrys Shea on wave soldering? Looks like she did not successfully post the article. We have emailed her on this, so hopefully you will be able to