Electronics Forum | Sat Aug 01 22:29:14 EDT 2009 | hohk
Here's the link to the image. It seems the forum's image feature is down? X-section view.. http://i672.photobucket.com/albums/vv88/hohk/X-sectionView.jpg Copper Strip with Adhesive Tape idea... http://i672.photobucket.com/albums/vv88/hohk/CoperStri
Electronics Forum | Fri Aug 21 04:43:14 EDT 2009 | ghepo
Hello, I suggest you visit the website http://www.analysispcb.com, where I found these information : PARAMETERS FOR DOUBLE “V” SCORING LEAD FREE LAMINATES Typ WEB Thickness, 1.6mm : 0.38mm (+.15/-0) "...Tg is not a good indicator of a materials’
Electronics Forum | Sat Aug 22 05:19:42 EDT 2009 | ghepo
Dear Eric, in my opinion this is a very complex problem, that require to know many details for answer. For example : 1) what about the PCB finishing ? Have you verify the quality of they ? 2) what about the solder paste (the exactly composition)? 3)
Electronics Forum | Sun Aug 23 07:03:09 EDT 2009 | ghepo
OK Eric, is difficult answer at distance without examine the PCB..., anyway in my opinion the problem is the PCB quality. There are two possibility : the crack is between solder and nickel or is between nickel and pad copper. In both situation the
Electronics Forum | Mon Aug 24 13:12:28 EDT 2009 | ghepo
OK Eric, maybe you're right. My suggestion is to proceed by exclusion. First perform the tape test. Is easy and without costs. You have used many similar PCB without problem, but from the same vendor ? Is my experience that in similar cases the qua
Electronics Forum | Wed Aug 26 05:24:42 EDT 2009 | ghepo
Ok Eric, finally we know that the problem should be the PILLOW (sincerely, your photo is not very clear) and not the crack of the joint. There is a big difference on the failure mode of the two defects... If the problem is realy a pillow I only ca
Electronics Forum | Thu Aug 27 13:14:49 EDT 2009 | ghepo
I have already told you that is not possible solve this problem by e-mail, without perform a detailed failure analysis. Also I have told you to procede by exclusion. Are you sure, by tests, regarding the PCB quality ? Are you sure regarding the solde
Electronics Forum | Fri Aug 28 08:52:13 EDT 2009 | duso02
Yes, you must thin Dow CC for any spray operations. We use Dow 2577 daily for multiple customers and we always thin it for spray operations and 2577 is considered medium viscosity. Dow recommends using up to 60% solvent (Xylene). Your 2620 is low vis
Electronics Forum | Thu Aug 27 10:22:59 EDT 2009 | dwl
We have an opportunity to purchase a Yestech YTV-1000 AOI machine. I am looking for opinions on how well they work and how they compare to the newer Yestech B3 AOI systems. We are a high mix, low volume EMS company. We do not currently have any exp
Electronics Forum | Wed Sep 23 03:43:31 EDT 2009 | d0min0
hello, we are profiling with the pcb each day - results are very good with a small delta we made another test board with TC only in the problem places - same good result we tried 500-600 boards on 12 zone machine - zero defects while on standard 6