Electronics Forum | Tue May 15 21:57:06 EDT 2001 | davef
Welcome!!! Where the hay ya been??? Sorry bud, were lining-up with your fab [it hurts me to say that, but when yer ] We used to dry pack with desiccants, also. Its probably an old MIL-STD-2073-1C requirement [er something like that]. We qui
Electronics Forum | Mon May 21 17:32:23 EDT 2001 | davef
I said: "Our electronic circuit board fabricators seal the boards in moisture barrier bags [MBB]. We discontinued the use of desiccant bags in these MBB because of concerns about the desiccant releasing materials that would affect the solderability
Electronics Forum | Mon Apr 12 19:28:26 EDT 1999 | Tom B
Netters, When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? 1. Kester 293 no clean 2. 2.1 C/s for 30s to 150 C 3. .5 - .7 C/s for 60s to 185 C 4. 1.5 C/s u
Electronics Forum | Mon May 05 22:24:17 EDT 2003 | jlipton
We are investigating a system, using 2-D matrix code, that will identify and track every PCB throughout our factory, starting from bare board. As a low-medium volume manufacturer, would labels or laser marking be more cost-effective? How difficult is
Electronics Forum | Wed Mar 12 07:33:40 EDT 2008 | callckq
Hi All, One PCBA failed test after went through the Shock Test(Vibration) and suspected to be BGA solder ball crack. We performed dye and pry and found PCB's pad lifted with red mark ink penetrate pad underneath, what does this mean? Can I say the
Electronics Forum | Thu Jul 06 13:36:37 EDT 2006 | SWAG
We've had much trouble with flex circuits. As previously mentioned, you must have local fids for the board or the BGA itself (if panelized). Other troubles we experience are drilled holes for pinned connectors. Unless the PCB manufactur has some w
Electronics Forum | Wed Dec 20 04:43:36 EST 2006 | greg york
Any decent flux would volatise off with the heat of the wave unless absorbed into the solder mask. Test this by trying to clean in alcohol or common solvent aerosol, if it does not clean then it is probably Mineral Salts from solder mask fillers. Ano
Electronics Forum | Tue May 06 09:38:41 EDT 2003 | blnorman
We use both labels and lasers to mark our boards. Since implementing the lasers, the downtime attributed to bar code labels on those lines have dropped to virtually nothing. We still have problems with the labels wrinkling during reflow making read
Electronics Forum | Mon Dec 18 23:24:50 EST 2006 | grantp
Hi, Yes, I would hate to resort to cleaning, but the product must be clean. We have been using palettes to keep most of the flux off the PCB, but there is still residue around the connectors. Does anyone suggest a good no clean flux to use with le
Electronics Forum | Thu Mar 31 12:13:28 EDT 2022 | cbart
That is a tough one because of package size I agree, as noted previously it would be good to know what the current PCB pad layout is. first thought does go right to an adapter board of course! is this a volume build or just 20-50 pcs? dead bug and ha
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830
.gif)