Electronics Forum | Thu Mar 08 09:00:50 EST 2007 | Rob
Thanks for the answers. Hi Dave, I'd love to use some of the durastone we have here, or some Durapol or Delmat (never used Glastic before though), however we need a compliant material for the blade to go into slightly, otherwise they tend to snap or
Electronics Forum | Sun Mar 25 15:38:07 EDT 2007 | Gibbon!
Couple of things. Type T thermocouples are solder friendly. However usually a header with screw terminals poses no problem as the temperature differential is nil. Getting thermocouple leads wet causes problems because two dissimilar metals + condu
Electronics Forum | Fri Mar 30 11:56:08 EDT 2007 | JD
We have had issues with using the ones from Best. The holes are not always cut correctly and the edges (inside the holes) are not well defined because of the kapton material they use maybe. Plus you leave the mini stencil on the PCB under the BGA whi
Electronics Forum | Thu May 17 09:53:14 EDT 2007 | mohdfazuwan
For ur information, this BGA machine was full utilize every day. I have more than 100 model to do profiling every week. Different PCBA with different thickness & material need different temp setting. currently i'm looking for profiler that more compa
Electronics Forum | Mon May 21 09:06:33 EDT 2007 | davef
Pat: Very descriptive SUBJECT choice. Surface tension: * Soldering and Surface Tension; Champion, JA; Physics Education, V 16, No 2, 1981, pp 98-100(3) Institute of Physics [We have not looked at this, so we cannot comment, but it seems like an appr
Electronics Forum | Fri May 25 13:24:38 EDT 2007 | mfgengr
I had a similar problem a long time ago. I eventually traced the problem to undercured solder resist. The flux was reacting with what was left of the uncured resist, leaving a white residue. We could not even hand scrub this off. The solution was to
Electronics Forum | Fri Jun 08 08:26:14 EDT 2007 | davef
Testing for solder mask cure: Search the fine SMTnet Archives, for instance: http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=15726 Residue after wave: Water in your wave soldering flux may cause your NC flux residue to go white. Indium W
Electronics Forum | Sat Jun 23 11:35:58 EDT 2007 | grantp
Hi, Yes, we just built a new plant, and used copper again. The stuff we cut out of the old building was copper, and it was fine without any issues. We lay it on an angle so condensation flows to an end, and can be periodically vented, and we take a
Electronics Forum | Tue Jun 26 10:41:32 EDT 2007 | slthomas
We had a cooler fail once, before we had any SMT. Auto-insert was at the far end of the building, at the end of the compressed air line. When the Unimod (dip inserter) sprayed the operator with water when the pneumatic table rotation motor fired up
Electronics Forum | Tue Jun 26 11:45:52 EDT 2007 | Frank
I certainly wasn't endorsing the use of the PVC piping that was installed prior to my employment there. Also, I recall that all the piping was above the ceiling tiles and regular air line hose was dropped along with the power cables. So there was l