Electronics Forum | Wed Aug 06 13:49:25 EDT 2003 | severs
Yes it is a conflict of interest. If the rep in > question is also calling on other contract > Assembly houses. If the rep is not calling on > other Ca's then I would say no. > Yes it is a conflict of interest. If the rep in > question is also
Electronics Forum | Thu Aug 14 09:35:47 EDT 2003 | patrickbruneel
Hi All, I enjoyed this discussion and applaud the quote from Stephen �following the followers�. I�m President/Technical Advisor in a flux and solder Mfg. Company and have so far resisted marketing lead-free and VOC free products, because at this poi
Electronics Forum | Thu Jan 29 15:30:41 EST 2004 | pjc
Rick, As I understand your comments, you do not need to clean off the flux residues? Then hot water and a little cleaning chemistry should do. However, there may be some reaction by the residual flux if not enough cleaning chemistry is used. There a
Electronics Forum | Thu Jun 24 14:34:13 EDT 2004 | tjensen
There are many factors that can lead to solder balls. Since you have just recently seen this start to occur, it is obvious something has changed in the product or your process. Since we don't have a lot of details about your process, I would sugges
Electronics Forum | Thu Sep 02 14:02:49 EDT 2004 | russ
Frank, We are currently running lead free for approximately 1 yr. now but no where near the volumes you have mentioned. We are about 5k units per month. I personally am in agreement with you as far as OSP. I also do not like white tin finish since
Electronics Forum | Sun Dec 25 18:54:04 EST 2005 | mariss
We are experiencing fracture problems with 0805 X7R capacitors. The capacitors seem to fail in tension; during hot-air rework they come apart in two pieces with the fracture near the metallization end. Only X7R SMT components are affected, C0G and Y
Electronics Forum | Tue Oct 24 09:52:35 EDT 2006 | SWAG
We are having the exact same problem! We do about 6 or so ROHS SMT builds. 5 are fine now but we had problems with most initially and 1 is trouble still. All boards are same material, same PCB manufacturer. Initially, when the delam. problem occu
Electronics Forum | Thu Jul 03 09:12:08 EDT 2008 | andrzej
Hi, if you do only contract services I`d advice own part numbering. All I can say is just try to create each cathegories which will contain other cathegories and so on. Applying this system will make some order in your stock. For instance : RETR020
Electronics Forum | Sun Aug 31 17:28:09 EDT 2008 | rezer
Hello federico, This is Reese. Yes, you can pick up tombstoned parts reliably with the M1. You cannot pick up lifted leads very well however. I have not tried other algorithms yet, just histogram analysis which is the standard method for inspecti
Electronics Forum | Mon May 09 16:44:33 EDT 2011 | dcell_1t
Hi, We have been struggling with an issue of non wetting on a QFP (Renesas - 256, Sn90Pb10) but the issue "desapears" sometimes for a while and then back again suddenly. This is the scenario: Component: QFP 256 / Renesas / Sn90Pb10 / 0.5 mm pitch S