Electronics Forum | Mon Apr 22 16:31:53 EDT 2013 | anvil1021
So, I was wondering how thick 2 oz. Copper is supposed to be? I have heard 60 microns and 70 microns, but the PCBs that we have that are supposed to be 2oz Copper are 68.5 microns, the Customer would like at least 60 microns, but what is the reality
Electronics Forum | Mon Apr 22 17:13:48 EDT 2013 | hegemon
Might want to double check my figures, but my notes have 2oz copper at 2.8 mils or 71.12 microns in thickness. 'hege
Electronics Forum | Tue Apr 23 15:18:02 EDT 2013 | davef
2 oz copper should be 2 oz per ft^2 thick. There is no relationship between thickness and copper weight due to the effect of processing. Since this is a painful way of thinking about things, ppl have reached a compromise and talk about 'nominal thick
Electronics Forum | Fri Dec 10 18:02:45 EST 2004 | Sam El.
I was wondering if anyone has had any experience with either the Esec Micron 2 or the RD Automation CDB-50? We currently have a Micron 2 (1997 build). We are using it for small batches of flip chip. We use the waffle pack feeder not the wafer loader.
Electronics Forum | Thu Oct 17 05:16:44 EDT 2013 | vincentdesilva2003
Anyone can help me how many percentage of blowholes and pinholes if i do the followings: 1. Increase copper plating thickness more than 25 microns. 2. Pre Baking of PCB to remove gassing by drying out the PCB's
Electronics Forum | Mon Jun 12 10:07:08 EDT 2006 | mkehoe@sipad.net
Can someone look this over and see if this helps?? ****************************************************** I read the e-mail threads and I think the respondents are all mixed up on the units of measure. the print reads: Gold Plate (80 mocroinches m
Electronics Forum | Mon Sep 11 00:31:13 EDT 2000 | rcsantos
Is there somebody who knows if there is a machine already available in market that can transfer die from wafer to waffle tray. This machine should a stand alone type or can be integrated to some P&P machine. What I'm trying to say is just like the on
Electronics Forum | Mon Sep 28 12:43:48 EDT 1998 | Manish Ranjan
Hi Everybody My company is looking to buy some precision measurement systems to measure the height of flip chip bumps (nominal height of 100 microns). We are looking for a resolution of about 2 - 4 microns. Any help would be appreciated. Thanks Man
Electronics Forum | Thu Nov 02 22:11:46 EST 2000 | Dason C
Please check with Fab house, what is the thickness of the immersion gold if the gold thicknesss is less than say 2.5 micron, you will found dewetting or open. It is recommend the gold thickness is around 5 micron. Good Luck Dason
Electronics Forum | Wed May 05 05:41:02 EDT 2021 | jineshjpr
Hi All, Need your suggestions on the below queries: 1. What will happen if the Au thickness maintained @ 0.5 to 1 micron (Where Ni Thick is within 3 to 5 microns) in 0.2mm Thickness FR4 PCB. 2. Is there any solder quality affcted during Reflow Solder