Electronics Forum | Thu Jul 17 11:34:35 EDT 2003 | pjc
� Center board support: - Stationary tension wire - Adjustable width and height position (manual) - Pneumatic raise/lower feature; extends through preheat and solder wave - Minimum board clearance on bottom preheater #1 is 63.5 mm (2.5 in.) with
Electronics Forum | Fri Aug 08 18:06:35 EDT 2003 | davef
Antistat sprays are a waste of time and money. These sprays just soaps disolved in water that absorb moisture from the air. Your minimum requirements: Conductive floor mats and wrist straps that are properly grounded. From there, consider using
Electronics Forum | Tue Sep 16 10:58:03 EDT 2003 | swagner
I am currently having a discussion with a pcb supplier about inadequate hasl thickness, we are measuring below 40 microinches of hasl when our spec calls for 100 microinches as the minimum. Our supplier came back with the statement the entire indust
Electronics Forum | Wed Nov 19 19:28:59 EST 2003 | bwet
We are looking for recommendations on reliability testing (thermal cycling, vibration, etc.) of BGAs AFTER being soldered to a PCB. Are there any standards that include such things as heating cycles (like a minimum of 5,000 cycles), ball-ball leakag
Electronics Forum | Mon Mar 29 11:49:44 EST 2004 | gregoryyork
White residue, probably nothing to do with the flux but was more than likely mineral salts from resist cure problem that are only soluble in Mineral Acids. No residue is the best IF resist is good, if resist issue's use low solids Rosin No Clean and
Electronics Forum | Mon Jun 14 11:44:23 EDT 2004 | Dreamsniper
I have boards with bad HASL application. First they're not even. Second some pad edges have no HASL and still remains bare copper. What's the maximum and minimum HASL thickness required for a good solderability. My boards are about 6 weeks old, I kno
Electronics Forum | Tue Aug 17 13:24:47 EDT 2004 | blnorman
We have parts that have electroplated tin over nickel. The mfg. assures us the minimum thickness of the tin is 5 microns. Cross sections have shown many instances of 1 micron and pits that go down to the nickel barrier layer. A request for thicker
Electronics Forum | Tue Nov 30 11:09:16 EST 2004 | fcox
Mesh opening size may be a factor in whether or not the paste will pass but only in very fine line deposition. Generally speaking, the printed line width and deposition thickness determine what mesh to use. The paste supplier will be able to tell you
Electronics Forum | Mon Dec 13 06:21:14 EST 2004 | Peppe
I work in electronic industry and I'm interested about the standard values of FIT (failure in time or useful lifetime) of soldering. In essenze my question is : how much time can work a good solder joint, before became fail ? Exist a minimum and ma
Electronics Forum | Tue Jan 18 12:41:14 EST 2005 | paulom
I am having some problems with regard to soldering of PBGAs. In the factory had high humidity. Can I make Bake in different temperatures of 125 and 40 degrees? Which the minimum temperature? How many times I can effect bake without damaging the com