Electronics Forum | Mon Jan 07 20:37:15 EST 2002 | davef
For soldered areas, we like to keep gold thickness substantially below the maximum you propose. Search the fine SMTnet Archives for our discussions on the topic of acceptable levels of gold with solder connections. Let�s fix this �no one seems be s
Electronics Forum | Wed Jan 09 15:24:49 EST 2002 | mregalia
Thanks Chris. As I was writing my last message our mailperson dropped off the latest issue of Circuit Assembly. It has an article on mixing SMT and COB on the same board. The author recommends as a compromise 10-20 micro inches of gold over 70-100 of
Electronics Forum | Fri May 17 10:53:15 EDT 2013 | davef
ENEPIG or Imm Pd? Concerns about palladium as a solderability protection are: * Palladium is more difficult to process in fab than gold * Palladium solder alloys can be brittle, similar to gold, without proper soldering process and/or specification/
Electronics Forum | Tue Oct 07 12:35:10 EDT 2008 | andy_pal
Hi All, I am using COB on my DOUBLE SIDED PCB. lastly we used Eletrolytic Ni / Flash Gold Plating. Our Boards vias Failed the UL corrosion Test. we did some cross-section analysis and found 10.75 �m of Nickel and 0.022 um of Gold and as the Process
Electronics Forum | Thu Jun 25 09:53:04 EDT 1998 | Earl Moon
Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. Mike Mike, You
Electronics Forum | Wed Jun 24 16:23:29 EDT 1998 | Justin Medernach
Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. Mike Mike, Your concer
Electronics Forum | Fri Jun 19 10:03:46 EDT 1998 | Earl Moon
Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. Mike Mike, We and ind
Electronics Forum | Mon Nov 09 09:44:22 EST 2015 | davef
Purpose. This describes setting-up a wave soldering system set-up for a new assembly design or checking a wave solder machine operation with a test board. Applicability. To be used for new design printed circuit assembles and during machine accept
Electronics Forum | Tue Feb 16 21:29:18 EST 2010 | actioncontrols
I predict you will have no problems with your soldering. Remember that all plating is only a few microns thick and quickly washed away by the molten solder. We have used white tin, immersion gold, OSG, etc. for quite a while with leaded solder and
Electronics Forum | Thu Oct 21 14:02:32 EDT 1999 | Ron Costa
We are a contract manufacturer currently building a job with IBM CBGA-255 devices and 20mil QFP's that are close to each other. We use a 6 mil laser cut and electro polished stencil with one to one apertures on the BGA's. The customer is experiencing