seperation of soldermask and pcb

Electronics Forum | Tue Mar 25 09:35:28 EDT 2014 | emeto

Have you tried to bake the boards before you process them?

seperation of soldermask and pcb

Electronics Forum | Tue Mar 25 10:31:05 EDT 2014 | sara_pcb

The boards are baked for 2 hours at 120 deg C Regards, R.Saravanan

seperation of soldermask and pcb

Electronics Forum | Tue Mar 25 08:29:33 EDT 2014 | sara_pcb

Please refer the attached jpegs, The problem is noticed after reflow soldering followed by conventional through hole soldering. Flux used one is MIL Std. Brush cleaning in IPA is followed after each soldering step. regards, R.Saravanan

seperation of soldermask and pcb

Electronics Forum | Tue Mar 25 11:25:18 EDT 2014 | horchak

The first impression I get is that the mask was applied over dirty or contaminated copper. What is the trace and land finish on the PCB? You also appear to have a wetting problem.

seperation of soldermask and pcb

Electronics Forum | Tue Mar 25 11:43:48 EDT 2014 | sara_pcb

It is Solder Mask on Bare copper, The land finish is HASL as per MIL-PRF-55110G which accepts trace of HASL as acceptable. Wetting is acceptable. regards, R.Saravanan

seperation of soldermask and pcb

Electronics Forum | Tue Mar 18 11:53:58 EDT 2014 | sara_pcb

Our contract manufacturing agency have procured pcbs from approved vendor. After assembly we found solder mask separated from the PCB on the epoxy area as patches. The top side is intact. also over the pcb tracks, the mask got damaged. In what c

seperation of soldermask and pcb

Electronics Forum | Wed Mar 19 08:38:13 EDT 2014 | davef

I can't picture much of what you're saying, not for nothing, I'm just not connecting. During assembly, solder mask can affected by heat and chemicals. Typically this would be during: * Soldering * Cleaning I will tell you this: Not to defend assem

seperation of soldermask and pcb

Electronics Forum | Tue Mar 25 13:55:05 EDT 2014 | horchak

Ok lets put it this way. If the PCB house used a high quality mask and properly applied it to a properly cleaned surface and properly cured it, then as Dave stated above there are only two things that can destroy it. Excessive heat and overly aggress

UPS and ROHS Compliance

Electronics Forum | Thu Jun 15 18:15:34 EDT 2006 | nickel

If you have time, download the free Practical Guide to Understanding the Scope of the WEEE and RoHS, you will find what they say about UPS. They consider UPS out from the field of application of RoHS. ORGALIME (Bruxelles)is the European Engineering

Pad and Stencil Design

Electronics Forum | Mon Sep 17 17:49:02 EDT 2001 | arzu

What about the material of the stencil? Nickel formed? stainless steel? even more materials are available, some with different ways to form the apetertures.

  1 2 3 4 5 6 Next

nickel and seperation searches for Companies, Equipment, Machines, Suppliers & Information

Blackfox IPC Training & Certification

Want to know where to find the best AOI system? - Read testimonials.
Reflow Ovens

World's Best Reflow Oven Customizable for Unique Applications
Panasonic CM402, CM602, DT401

Easily dispense fine pitch components with ±25µm positioning accuracy.


SMT & PCB Equipment - MPM, DEK, Heller, Europlacer and more...