Electronics Forum | Wed Oct 02 18:18:58 EDT 2002 | davef
The steadfast rule of thumb is: In order to get reliable reflow, you need to be at or higher than [liquidus + 20�C] for about 5 to 10 seconds, rather than those old "60 seconds above 183�C" guideline. This provides for setting your peak based on the
Electronics Forum | Thu Sep 26 14:43:43 EDT 2002 | Jim M.
unsure of what solder spec. your working to?.IPC/EIA J-STD-001C, Section 9.2.4 clearly states dull, matte, gray or grainy appearing solders are accpetable depending on your process and if the acceptability of the neaxt paragraph is met.IPC 610 and J-
Electronics Forum | Tue Sep 18 15:35:23 EDT 2001 | jschake
A laser cut stainless steel stencil was used exclusively for the evaluation of the complete 0201 assembly process, which addressed printing, placement, and reflow. However, I have also conducted off-line 0201 print tests using a nickel electroformed
Electronics Forum | Mon Jul 19 11:11:18 EDT 1999 | Wolfgang Busko
Perhaps a little hard to find but is there anyone who uses a vapor phase process to solder populated card with BGAs. I am interested in the success rate of such a process. It is obvious that the throughput is reduce vs a convection oven but still t
Electronics Forum | Thu Oct 12 22:16:59 EDT 2000 | Dreamsniper
Hi Guys, I'd like to share this to all of you...you can start playing with the rests...Stated prices, if not indicated, are in Aussie $ or Singapore $. Stencil Printing Adhesive Pros a) Less Capital Equipment Cost (Short Term). In reality it is f
Electronics Forum | Wed Oct 04 14:54:46 EDT 2000 | Sean
I feel Woldgang poses an interesting question. It seems you have already decided that dispensing is the path you wish to take. Yet can you tell us why? Is there a flexibility vs. throughput arguement here? Justification of dispense via the cleani