Electronics Forum: no clean flux (Page 1 of 210)

cleaning of no clean flux

Electronics Forum | Wed Aug 10 07:55:21 EDT 2005 | ajaydoshi

we are using heareous F381, F352 no clean solder paste. specially in qfp for high frequency board we observe that cleaing / removing of ' no clean flux 'is require. if we do not clean same most of time after all test & envioumental test it shows pin

cleaning of no clean flux

Electronics Forum | Wed Aug 10 08:10:39 EDT 2005 | davef

Comments are: * Sounds like it's necessary to clean "heareous F381, F352 no clean solder paste" in your application. Consider a paste that may be better suited to your application. * If you're cleaning "low residue flux", consider using an organic ac

cleaning of no clean flux

Electronics Forum | Wed Aug 10 08:53:45 EDT 2005 | jh0n!

Wasn't aware of that. We're using a no-clean with RF pcbs, and that's something to bear in mind for the future - thanks.

cleaning of no clean flux

Electronics Forum | Wed Aug 10 17:19:24 EDT 2005 | Steve Stach

The propensity for flux residues to cause shorts can be increased in humid environments where water molecules hydrate the surfaces. At high frequencies, electrons travel on the surface of conductors/insulators, increasing the likelihood of shorts in

no clean flux + wave soldering issue

Electronics Forum | Tue Sep 02 14:59:41 EDT 2008 | hermes

if two boards with different solder masks give different results on flux residue level after soldering with the exact same machine settings than it is clear that one of the solder masks is not compatible with your no-clean flux. could be the solder m

no clean flux + wave soldering issue

Electronics Forum | Wed Aug 27 15:49:43 EDT 2008 | grics

I think WML ought to have some photos on how to do this...

no clean flux + wave soldering issue

Electronics Forum | Wed Aug 27 22:54:44 EDT 2008 | omid_juve

what is WML ? can you please explain more

no clean flux + wave soldering issue

Electronics Forum | Thu Aug 28 16:21:23 EDT 2008 | realchunks

Larry, I'm seeing a pattern here of you and fire!?!?! What gives?

no clean flux + wave soldering issue

Electronics Forum | Thu Aug 28 09:30:20 EDT 2008 | patrickbruneel

Omid, No-clean fluxes need to be used right out of the can without thinning. In the past with RA and RMA fluxes you could adjust or thin them to your desired density because they had plenty of solids up to 30%. No-Clean fluxes have a lot lower solid

no clean flux + wave soldering issue

Electronics Forum | Wed Aug 27 14:58:21 EDT 2008 | omid_juve

we have problem in setting the density of a no clean flux for using before wave soldering . first we dilute the flux but we have many short circuit problem between the pads of edge connector,then we densify the flux all the short circuit is removed b

  1 2 3 4 5 6 7 8 9 10 Next

no clean flux searches for Companies, Equipment, Machines, Suppliers & Information

2024 Eptac IPC Certification Training Schedule

High Throughput Reflow Oven
Selective Soldering Nozzles

Training online, at your facility, or at one of our worldwide training centers"
SMT Machines

World's Best Reflow Oven Customizable for Unique Applications
used smt parts china

Nozzles, Feeders, Spare Parts - Siemens, Fuji, Juki, Yamaha, etc...
High Throughput Reflow Oven

Reflow Soldering 101 Training Course
PCB Depanelizers

Training online, at your facility, or at one of our worldwide training centers"