Electronics Forum | Wed Oct 27 19:50:59 EDT 1999 | chris

Hi What is the possible cause of non-wetting of solder paste to the gold land pad. What we observed in the surface of the non-wet pad is an organic FM, and using FTIR we found out that it is a flux. It is possible that the cause of non-wetting is

Re: non-wetting on gold land pad

Electronics Forum | Thu Oct 28 09:25:35 EDT 1999 | Dave F

Chris: Typical non-wetting causes are: * Poorly controlled soldering process * Incorrect material * Surface contamination * Insufficient preheat * Misapplied solder mask * Shadowing Without intending to insult you, all of the causes of non-w

Solder paste height checking

Electronics Forum | Wed Mar 30 01:01:10 EST 2005 | vicknesh28

All, Has there been any finding from the component point of view in terms of non wets after reflow and if yes, can anyone share what was improved on the component to reduce the non wet defective levels. What would be the contribution from the compon

Re: non-wetting on gold land pad

Electronics Forum | Fri Nov 05 10:01:04 EST 1999 | Dave F

Chris: You can have more than "one question!!!" Anyhow, yes crappy solder paste can cause non-wetting, but before you go there understand why the paste is wetting some surfaces, but not others. Ta Dave F

Re: non-wetting on gold land pad

Electronics Forum | Thu Nov 04 21:36:36 EST 1999 | chris

Hi John, Thanks to your reply, just one question is it possible that the solder paste ( flux material )applied to the pads cause the non-wet. regards Chris

Component non wetting

Electronics Forum | Wed Apr 21 21:50:28 EDT 2004 | adam

Hi I recently having problems on the components having non wetting on the flex circuits. The profile that I am using is according to the solder paste suppiler recommended. Can anyone pls. advise? Regards

BGA non wetting

Electronics Forum | Wed Sep 15 20:59:23 EDT 2010 | genesan

hi All, Here i snap shot previous PCB(HASL) and current PCB(Immersion Silver).Base on the photo it could be PCB oxidize cause the non wetting?


Electronics Forum | Thu May 16 22:37:22 EDT 2002 | xzinxzin

anyone experience to solve the non-wetting on Microleadframe packages component terminal sides. 1)I test the components solderbility in dip and look test, in solder pot at 240 deg C,the wetting on the sides is ok. but I run on mass production in refl

Non wetting on fine pitch product

Electronics Forum | Thu Sep 07 03:47:07 EDT 2006 | vicknesh28

I have been getting non wets on fine pitch QFP packages on random leads during reflow process. I noticed that every time there is some flux residue left between the non-wet lead and the solder pad. No residue was not observed on the rest of the good

Non-wetting on QFP lead

Electronics Forum | Sun Nov 25 20:47:44 EST 2001 | Yngwie