Electronics Forum | Tue Jul 11 11:18:06 EDT 2006 | dougs
Thats a good point SWAG, i'll look into that for the next run of these. cheers
Electronics Forum | Wed Nov 17 20:11:29 EST 2021 | dwl
is there flux on the board? are you probing a test point or a soldered pad? is the probe hitting the right spot?
Electronics Forum | Fri Feb 14 11:45:11 EST 2003 | SV
I was wondering if you guys had any experience with a distributed coverage Test and inspection strategy (Awaretest Xi) and could point me to technical studies in the field. thanks
Electronics Forum | Thu Jul 14 10:00:21 EDT 2005 | chunks
Any one using SPC to monitor their wave solder process? My point is collecting defects and using a scatter plot is useful but only after a problem occurs. SPC's true function is to warn of impending problems that are about to occur. Can SPC really
Electronics Forum | Mon Dec 19 12:21:09 EST 2005 | Amol Kane
from what i know, Tg is important from thermal stresses point of view. board warpage increases greately when Tg is exceed
Electronics Forum | Thu Jun 22 00:16:24 EDT 2006 | Gman
Hello, Has anyone had issues with voiding while using Imm Silver PCB finish. Does thickness of silver, contamination of the plating bath or other factors if you come point out cause voids due to the plating.
Electronics Forum | Tue Sep 29 10:53:42 EDT 2015 | marlyn
Hey there fellow people with SMT issues... What's the proper procedure for soldering through-hole headers on the back-side of the PCB (pins poking out on same side as SMT parts)? ( Yes - I did the SMT side first and am now faced with LOTS of pin-poin
Electronics Forum | Wed Jul 24 09:54:49 EDT 2019 | amitthepcbguy
Typically, the reliability of PCBs suffers significantly due to the increase in aspect ratio. It is not preferred to opt for high thickness boards. However, I would like to point out that your assumption seems to be wrong as board layers do not direc
Electronics Forum | Fri Dec 16 18:37:10 EST 2005 | mdemos1
Hi. I am trying to understand Tg and how it relates to reflow. With the higher temperatures of lead free, we have been looking toward laminates with a Tg of 180 instead of the current 140. My question is a little more general. In either lead free