Electronics Forum | Thu Apr 19 15:22:34 EDT 2001 | jdtpfacreate
Spanky, It sounds like you are looking for a recipe to use when you do get an assembly in that has 0201's on it. We have worked with our customers worldwide in the development of the process to use 0201's. Most equipment manufacturers out there
Electronics Forum | Mon Nov 27 12:13:39 EST 2000 | rabell
Dave, this is a massive question, and if you have any hard data on these issues, it would be wonderful if you could share it. The best I can offer is some indication of our experiences from contacts in the industry. Keep in mind as well, that we ha
Electronics Forum | Tue May 08 13:39:27 EDT 2001 | genny
Thank you for your response. I have been told that x-ray strength is finding solder volume and pattern root cause defects, and will catch a high % of them - opens, shorts, insufficient solder, and missing components(shape of solder on pad w/o lead i
Electronics Forum | Sat Feb 12 10:15:40 EST 2000 | Rick Thompson
I have to agree with Michael's comments. We've been evaluating systems for a month or so. There's a pretty wide range depending on what you're looking for. I'd say the first thing needed is to define your expectations. Are you looking for solder in
Electronics Forum | Sat Oct 09 09:07:48 EDT 1999 | Brian
| | | Can anyone tell me the formula/method to determine | | | the amount of weight that solder's surface tension can support. | | | (ie: Maximum weight of components soldered onto a bottom side | | | of a board during a top side reflow on a Paste/Pa
Electronics Forum | Sat Oct 09 09:18:21 EDT 1999 | Dave F
| | | | Can anyone tell me the formula/method to determine | | | | the amount of weight that solder's surface tension can support. | | | | (ie: Maximum weight of components soldered onto a bottom side | | | | of a board during a top side reflow on a
Electronics Forum | Sun Oct 10 17:50:00 EDT 1999 | JohnW
| | We've recently encountered this problem where one of our .050" pitch BGA's were reflowing at the wave thus causing shorts... The board was profiled with probes stuck to a QFP solder joint, an 0603, and one of the BGA joints. There was an almost
Electronics Forum | Wed Oct 06 08:49:36 EDT 1999 | Dave F
| | | | Can someone suggest what material I have to use to protect components by electrical discharge on ptfe based boards? | | | | It should have high resistivity, thermal stability (-40 +70 'C),perfect adherence on ptfe... | | | | Many tahnks | |
Electronics Forum | Thu Sep 30 15:06:05 EDT 1999 | Dave F
| Guys & Gals, | | I am at present instigating a formal method of recording and tracking any "process" trials that we may wish to run, such as a new paste, different packaged device etc; | | I started with a simple form.....too simple, but now I th
Electronics Forum | Tue Sep 28 11:25:32 EDT 1999 | Scott Cook
| | | | | I'm trying to start a small SMT contract shop and I need | | | | | assistance in selecting equipment. Quad seems to be the | | | | | leader but if there is something else out there that can | | | | | better suit me please let me know. My s