Electronics Forum | Fri Aug 04 08:28:20 EDT 2006 | Rob
Hi Joe, Try: S03X7C-56M from koki - http://www.ko-ki.co.jp which has cobalt in it to extend tip life or: SN100C from Nihon Superior, which is a nickel stabilised alloy that also extends tip life. The Koki solder flows better that any other leadfr
Electronics Forum | Mon Jul 30 10:17:26 EDT 2007 | davef
immersion ...easily changes color.. See that's the GREAT thing about immersion coatings. If they change color, they probably will not solder well. Try that with other coatings.
Electronics Forum | Thu Jan 29 11:30:56 EST 2009 | rgduval
As others have said, you'll have some difficulties getting good reflow on pb-free out of a 3-zone oven. We did it with a 4-zone for awhile, but only had really good success on low thermal density boards. That said, you should definitely check your
Electronics Forum | Tue Aug 31 19:50:44 EDT 2004 | davef
To take our turn at keeping everyone else on the straight and narrow. For more on lead contamination of no-lead solder, look here: http://www.aimsolder.com/techarticles/Lead%20Contamination%20in%20Lead-Free%20Electronics%20Assembly.pdf [We apolog
Electronics Forum | Wed Jun 16 11:24:09 EDT 2004 | larryk
I learned yesterday that Kester is using a different color on their products. They thought that other manufactures would also follow their lead in this.
Electronics Forum | Mon Jun 14 22:36:52 EDT 2004 | Ken
I hear ya Ray, but I have standard (automatic) solder dispenser that are 700gram modules. Jars have other issues that I have migrated away from... I like your idea of slaving the paste bar code label to the board scanner....
Electronics Forum | Tue Jul 12 16:03:09 EDT 2005 | autoequip
I have recently been testing a new Iron that will be introduced on the market soon. The temp drop is coming in at 30c versus most other irons I have tested drop about 70c the tips are elctroplated and designed for lead free we have been very impresse
Electronics Forum | Wed Oct 19 20:04:06 EDT 2011 | warwolf
yeah I’ve tried to go down the road of internal recycling but the company carnt justify spending 20k on a machine that does it. Ah but where still onto it in other places though our SMT department has very minimal wastage on solder paste as we have b
Electronics Forum | Fri Jan 14 08:42:47 EST 2005 | Jim Zanolli
We are performing testing for lead free connector finishes. We want to run solderability tests on a series of lead free connector plating options in a series lead free PCB's. I need some advice on the most popular lead free PCB finishes. I am aware
Electronics Forum | Tue Jun 01 16:10:44 EDT 2004 | raylawre
Would like to know what people are doing to differentiate their lead and lead free environments in their production areas. How do you keep it separated? What, if any, visual colors do you use to indicate a lead free area? Gray? Green? For instance, w