Electronics Forum | Mon Aug 09 15:49:16 EDT 2004 | celldude
We have definitely seen money saved. There is a lot less rework after reflow. Money is also saved in overtime. for example...when we are building a first article board with many placements, it is not always possible to get the first board through the
Electronics Forum | Tue Sep 14 08:46:31 EDT 2004 | scombs
I'm currently working for a OEM that has 700+ stencils in house and we received 30 to 40 stencil a month. We recently switched to a no clean process which is causing the stencil part numbers to disappear from the stencil frames due to the saponifier
Electronics Forum | Fri Oct 21 01:50:54 EDT 2005 | Jesse Mullen
Hi, i was just browsing the net i seen your post. I offer laser transfer machines that can transfer full color on just about any type of material. For more info go to http//ia.local.yahoo.biz/fullcolorgraphics also you can e-mail me, i mainly do prod
Electronics Forum | Wed Nov 10 15:18:15 EST 2004 | Dave G
Let's go for Ugly..... I've used these in the past for attaching connectors to boards and tabbed Transistors to extruded Aluminum heatsinks with mixed results. The concept is great but, in practice there are some headaches to deal with. We've gotten
Electronics Forum | Wed Jan 12 21:37:04 EST 2005 | KEN
How thick is this pallet? 6mm, 8mm, 10mm? I would look at: Make sure you're pot height is correct (lead clearance). If you are burrying the pallet in the fountain, your going to "push" a large volume away. The solder "push" should not plow over t
Electronics Forum | Wed Jan 26 15:38:46 EST 2005 | TomA
Jay, Yes, we did assigned new part numbers for our lead free components. Our concern was how do we know that this component is lead free. New part numbers was our only way. It made the component engineers cry, but offer them a box of Krispy Kreames
Electronics Forum | Tue Feb 01 09:54:23 EST 2005 | jbrower
Hi Frank, we're still going to go with FR4 as our prefered material. Our board thickness is .062. We use an on shore and off shore vendor. Prototron I believe offers an immersion tin and excellence in china? offers an immersion tin finish. We fou
Electronics Forum | Sat Feb 12 13:40:27 EST 2005 | etienne
As I was explaining in my thread, the things that you have to look for when buying an AOI is the false calls rate (which you described perfectly) vis a vis the money and time you want to spend. We bought our machine after that we evaluated some. As y
Electronics Forum | Fri Jan 28 12:29:01 EST 2005 | Bob R.
We use the exact same method Chunks outlined for evaluating just about anything we're going to roll out worldwide, whether it's a material or a machine. List your factors (print speed, solder spread, etc), assign each a weight, evaluate each paste a
Electronics Forum | Wed Feb 02 22:10:30 EST 2005 | T2
Higher Tg values are only one thing to look out for. Two other things that are very important to watch are the Td or Decomposition Temperature (the temperature that the epoxy actualy starts to break down), and the CTE for the material. Some Tg 14