Electronics Forum | Thu May 28 08:56:12 EDT 1998 | Earl Moon
| I have a component that is glue cured on the bottom of a pcb. The component is a 1206 size jumper. It is made up of iron/nickel alloy. The problem I am having is that the part will fall off the board during wave solder. Is the component not abl
Electronics Forum | Fri Apr 17 14:08:44 EDT 1998 | Earl Moon
| Currently I am in the buisness of soldering bare die to the top surface of a copper heat sink. Is any one else | have some exprience in this process that can help. We heat a copper slug through a contolled atmosphere, place a preform then a bare
Electronics Forum | Mon Apr 13 17:03:40 EDT 1998 | EFData
We are having some difficulty soldering a 240 pin Altera device. We use Alpha WS-609, a very generic profile for that solder paste, and a 6 mil stencil with laser cut apertures (1:1 ratio). This is a 20 mil pitch device (aperture size is 10 mils X 75
Electronics Forum | Sun Mar 01 15:52:13 EST 1998 | Earl Moon
| From several months I am investigation about the VOIDS PERSENCE and his important as reliability. | One question now is : | It is possible that on the BGA components the voids are already present into the balls, before the mounting on the pcb ? | I
Electronics Forum | Wed Dec 31 08:55:09 EST 1997 | justin medernach
| Has anyone had any experience with thermal shocking | and cracking of SMD capacitors during the rework process? | My company was advised to preheat capacitors to 125 C | at a rate of 2 C/sec before replacing them onto boards. | Would this maybe
Electronics Forum | Mon Aug 27 10:58:44 EDT 2001 | Ryan Jennens
Steve- We had the same trouble with 0805 Panasonic film caps. We had some tombstoning and open solder joints (non-wetting). We found two problems...like you, we changed our pad design to meet their recommendation. Also, they were able to suppl
Electronics Forum | Mon Feb 11 13:28:36 EST 2002 | stepheno
We have some BGA's that don't solder very well. They weren't properly stored in regards to moisture protection. The balls look dull and rough. After reflow there seemed to be a diffinate line between the balls and the solder on the PCB's. I think
Electronics Forum | Mon Feb 11 21:54:14 EST 2002 | davef
LONG TERM Your plans to buy a vaccuum bag resealer and a batch drying oven sound good as you say, but you�re correct. They will not help with this current situation. SHORT TERM If your connections are clean, free of pits and holes with a smooth,
Electronics Forum | Tue May 14 14:48:33 EDT 2002 | fmonette
Hi Dason, Here is some relevant information that you might find useful : J-STD-033, section 7.1.2.2 Dry Box : "Components may be placed in a dry box, capable of maintaining 25+/-5C and less than 10%RH. Nitrogen or dry air may be used." In other w
Electronics Forum | Tue Jul 30 08:38:55 EDT 2002 | dasal
Truthfully, there are pro's and con's for both technologies. (put cost of ownership aside for one moment) Nitrogen won't dry humidified components as rapidly as a desiccant dry box. I'm talking about a self regenerating dry box that uses molecular s