> What about designators? Using gerbers to program > a pnp machine was always a last resort to be done > only after much complaining and begging for > proper CAD data. Back in the day I used UniCAM to > program a mydata. After gett
Electronics Forum | Wed May 19 20:39:28 EDT 2021 | kumarb
Elissa - SMTWenzhan ? She is great !! Have purchased many oddball and common parts from her including belts, filters, grease, etc. BTW - We placed 01005 using a nozzle she sold us with our Emerald-X. Unbelievable !! Granted the pick was hit or miss
Electronics Forum | Fri Jan 06 00:03:10 EST 2023 | SMTA-64419298
Hello Evtimov, sorry...just saw post as I was looking through list...a bit late. I don't know if you ever got your answer. IPC-4552A covers EniG finishes and suggested shelf life. I've referred to these doc's quite a bit. Good spec's ! Yes, I beli
Electronics Forum | Sat Jul 22 13:20:35 EDT 2023 | shrikant_borkar
Dear Abhishek, I too got the opportunity to investigate this defect Lift lead for SOT. Lead lift in IC, and SOT can occur due to various reasons. Here are some possible reasons for lead lift and ways to avoid them: During the assembly process, mecha
Electronics Forum | Tue Mar 21 20:25:30 EST 2000 | Dave F
John: What�s the matter? Free gold � good thing for you, bad thing for your supplier. :^) Pre-tinning of gold plated leads is important to: � Prevent gold embrittlement of the solder joint � Determine if the leads are solderable prior to assembly (
Electronics Forum | Sat Oct 02 03:27:52 EDT 1999 | Brian
| I am currently in the middle of a company wide war and I'm looking for data (AMMO). Here are the problems: | | 1) I am looking for anyone who has done or seen any reports on Thermal Shock to smt parts and/or via holes caused by Soldering Irons at
Electronics Forum | Fri Sep 17 09:54:40 EDT 1999 | Brian
| | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a
Electronics Forum | Fri Sep 17 10:09:17 EDT 1999 | Earl Moon
| | | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However,
Electronics Forum | Tue Jul 13 14:19:00 EDT 1999 | JohnW
| | | Hi, | | | | | | I need some urgent informations on stencil design guidelines on how to perform epoxy printing on 0603 and 0402 components. Could anyone help? ( Reflow process is not possible because of some other constriants) | | | | | | Sec
Electronics Forum | Tue Jul 13 14:25:57 EDT 1999 | Earl Moon
| | | | Hi, | | | | | | | | I need some urgent informations on stencil design guidelines on how to perform epoxy printing on 0603 and 0402 components. Could anyone help? ( Reflow process is not possible because of some other constriants) | | | | |
PCB Libraries' "Footprint Expert" suite uses CAD LEAP(tm) Technology to greatly simplify footprint and 3D STEP model creation; it is used by tens of thousands of PCB designers and engineers all over the world.
Other / Media / Publisher / Online Resource / Consultant / Service Provider
24654 N. Lake Pleasant Pkwy
Peoria, AZ USA
Phone: 847-557-2300
.gif)