Electronics Forum | Tue Dec 13 02:45:49 EST 2005 | hacuong
Hi, Pls give me some guide lines on standard parameters of Wave soldering technology or intruct me where we can find it. I have some issues with quality after wave soldering machine (Speedline-electrovert)and would like to verify our profile whether
Electronics Forum | Mon Jan 09 05:14:56 EST 2006 | abhinavajmera
Hi all, I want to know the possible causes of poor paste release in stencil printing process if the same brand and part number of solder paste that has been used successfully is being used with a set of process parameters which worked before. Other t
Electronics Forum | Thu Jan 19 11:04:08 EST 2006 | Mike Konrad
No, there are no issues with mixed lead / no-lead post-reflow cleaning. No-lead is a little harder to clean so be sure you use the appropriate parameters and cleaning chemical. The only potential issue is if you mix up the boards after cleaning,
Electronics Forum | Wed Feb 08 08:05:51 EST 2006 | amol_kane
thank you for the reply.....this reinforces the same info about SAC305 that i had reviewed in other papers. Since this is an inherent property of SAC305, i am assuming 1. Wave parameter (temp/time) tweaking will not mitigate this? 2. what is differ
Electronics Forum | Mon Feb 20 17:12:54 EST 2006 | mark
Hallo all, I have recently had possibility to work with DEK265. I have met with problem poor print definition (no sharp edges). I used stencil 150 thickness, metal squuegees. I moved than the same stencil, squeegee and parameters to DEK nifinty and
Electronics Forum | Tue Feb 21 14:02:25 EST 2006 | paligora
Hi People I will need some help on basic things really, we are replacing the existing solder pot with a lead free capable solder pot, but what are the other parameters that we need to look in to, to be able to achieve good quality soldering on the sa
Electronics Forum | Wed Feb 22 08:01:42 EST 2006 | INGE
We have a new SMT line, our customers are asking us the validation of the process. Not only the validation of the resulting assembled board (solder joint...) but also a validation of every single machine in the line (ex. stencil printer...). For exam
Electronics Forum | Fri Mar 17 07:42:51 EST 2006 | vicknesh28
Copper is the base material for the lead. It's tin/lead plated. I finally got profile. Here are the parameters" Peak : 219 Max (+) Slope : 2.29 Max (-) Slope : -1.94 Time above 200 deg. C : 50s Time 140C - 160C : 126s Additional info : Stencil thic
Electronics Forum | Wed Mar 22 03:00:09 EST 2006 | meritajs
Hi All, We have problem with Zevatech FS-730 This machine shows error E202062: "System error: T axis of head: Parameter error when T axis performs PTP action.(Kind of unit)" and it stop running. It does not pick up components. At low speed it works s
Electronics Forum | Sat Mar 25 16:05:13 EST 2006 | loz
Hi, sounds unusual if your profile is accurate that you have so many residues. Had a similar problem before with no clean flux and with various flux manufacturers, and all residues were down to excess flux. This does not help your case though. How a