Electronics Forum | Mon Aug 08 08:32:42 EDT 2016 | emeto
Just get a regular scale(small thin one - like a scale for kitchen). Mount it over a PCB and simulate placement with certain force. Hold the nozzle down for long time in order to register accurate reading from the scale. Then, just change parameters
Electronics Forum | Thu Sep 08 13:07:18 EDT 2016 | claudea2
Hello Bob, we changed the nozzle z parameter until we got limit errors and backed up 1 mil. There was a slight reduction in the limit errors on the pickup of the component but it is still a problem. With the mod code we adjust the soft z height to ab
Electronics Forum | Thu Sep 08 15:45:21 EDT 2016 | claudea2
Thanks Bob, I will change the z-rod just to make sure. It is a tall part read at 180. The nozzle height bugs me because we have 3 machines and the first one has a nozzle height of 238 while the 2 others around 200. I am thinking this parameter may ad
Electronics Forum | Mon Oct 17 12:18:04 EDT 2016 | intro
If I remember right you must go to secret screen . There you can change parameters of machine including language. You can find it in old posts: secret screen or panasonic password. one example for spp-g3 printer is: Request - F8 - F1 - F7 - shift - S
Electronics Forum | Tue Oct 18 04:12:09 EDT 2016 | dmmitry
Communication parameters is correctly. DB25(Male) to DB9(Female) wiring as is manual, lenght 1m, shielded. When i try read mcf CSMUTB program stoped with error "CSM not respond" or "Cant established communication", CSM84 display 125 Communication err
Electronics Forum | Tue Jan 10 02:17:29 EST 2017 | soldertraining
Hi ! I am also looking for the same and I am aware of this little like the -selective solder machines are generally cheaper to run due to the reduced amount of flux and solder being used and it’s possible to use a solder with no silver content and st
Electronics Forum | Tue Dec 27 06:52:34 EST 2016 | luciano
Thanks for your advice. I've tried setting the temperature up and even measuring the temperature at the wave itself but had no luck at all. I've also tried using temperatures going from 245 ºC up to 260 ºC. The amount of flux was adjusted as well a
Electronics Forum | Mon Feb 06 22:38:46 EST 2017 | david_chiu
No matter in selective soldering or wave soldering process, higher pot temperature and longer wetting time can increase IMC thickness and joint strength(reliability), but as Daivf said, you need to care if the DIP component and bare PCB was damaged b
Electronics Forum | Fri Apr 07 01:39:03 EDT 2017 | tsvetan
This parameter is in the component library, you do not change the force but the time when to start air blow. It's described in SM482 administration manual in component library programming IIRC. For what component size you want to do this change? In t
Electronics Forum | Thu Apr 20 02:27:11 EDT 2017 | pavel_murtishev
Mile, Please tell me more about your soldering process: - Are soldering process parameters the same for all three pins? - Is unsoldered pin connected to thermal heavy copper polygon? - What is your board surface finish? HASL? - Sn/Pb or LF process?