What works in Alaska will probably not work as well in Florida. We have solder paste vendors give us direction with their specific paste, but we also impart our required process parameters on their paste. For instance, here in Alabama in the summ
Electronics Forum | Fri Feb 20 15:46:44 EST 2004 | russ
Kinda what I thought, Ken, what would the parameters be relating to sphericity, flux, etc... We use type 3 63/37 usually watersoluble but for this I think I'm gonna have to use no-clean paste. When you say it can be done, what exactly does that
Electronics Forum | Mon Jul 12 05:03:30 EDT 2004 | itamar
hello ! my name is itamar and i need information about pcb laser marking machines. my knowledge in this field is limited and i would be grateful to know the important parameters that one should check before buying such a machine. i got several propos
Electronics Forum | Fri Aug 20 11:34:11 EDT 2004 | soease
Hi Grant, sly again. I was searching for some infos about Auto-SIR, and I found something that may interrest you; Concoat, wich is the company who sells Auto-SIR systems, also has profiling tools and they seem to have a more powerful software to ana
Electronics Forum | Mon Oct 04 11:47:00 EDT 2004 | HOSS
We are trying to deploy an Ionograph cleanliness tester and wanted to know what others are using as a standard test sample. My desire is to run the test on a weekly basis using the same medium complexity assembly. We plan to use the testing as a pr
Electronics Forum | Tue Oct 05 17:37:21 EDT 2004 | mikecollier
We currently use a KIC 2000 system to profile on our oven and create our recipes. I had a customer in today reviewing our profiles, and he had concerns that we were exceeding 4 deg. c/sec. on our profiles. The process window parameters that we use
Electronics Forum | Fri Mar 11 11:40:23 EST 2005 | JB
If there is an empty pocket at the pick up position, because a component "fell off" then the pick and place machine will attempt to pick up more components from the same feeder an "x" amount of times, depending on your component parameters, then it w
Electronics Forum | Wed May 18 07:22:06 EDT 2005 | davef
Wire bonds don't stick when bonded * Check pull and shear strength. * Depending on point of failure, review parameters. * Listen during bonding, if there is a high pitch buzz, there is vibration in the system somewhere, "seek and destroy". * Get the
Electronics Forum | Fri Jul 15 18:21:55 EDT 2005 | dggjr
We have Kester 256 no-clean spec'd as an alternate paste. I bring some 256 in occasionally to make sure it still works as a backup. The last batch I brought in was bridging like crazy. Scraped it off the stencil, put our regular Alpha back down an
Electronics Forum | Thu Jul 14 11:52:16 EDT 2005 | davef
Sure you can use SPC charting on the wave setup parameters to warn of impending problems. Examples of useful points of analysis are: * Dwell * Temperature * Pot analysis Certainly there's a range of other process controls that could be monitored.