Electronics Forum | Wed Jul 02 13:26:50 EDT 2003 | Terry Saunders
Hi, Terry!� Espi on our staff passed on your request to me.� I have attached a list of companies that offer previously used equipment.� You may want to try one of them.� You can also post this question on our Web site at http://www.smta.org.� Click o
Electronics Forum | Wed Sep 15 14:06:40 EDT 2004 | frankR.
Hi Rick, Last year I've test about 15 different solder paste. To procede, I've started with different tests listed in different brochure including IPC. At the biginning, I had 15 different tests to do and at the end ( for the last 7 product ) I've
Electronics Forum | Fri May 27 14:15:21 EDT 2005 | ve7khz
Hi Folks, Starting a second SMT line this year and it's been (too) long since I have looked at newish machines and I am in need of some assistance with P&P machine selection. Here is what we currently have: Panasonic CM-202 chip shooter 216 8mm reel
Electronics Forum | Sun May 29 17:36:11 EDT 2005 | MikeaJ
Dear JMT, I have read your reply, and you have one small valid point. There are times when you should call Technical Support. It is not for us to judge when each individual calls upon that resource, allow me to note a few points: 1. You can't always
Electronics Forum | Sun Mar 12 01:58:44 EST 2006 | grantp
Hi, We have been soldering lead free BGA's onto products with lead based paste, and we have had no increase in defects at all. We have used a standard lead paste profile, so we are not altering the temps anything from what's recommended by the paste
Electronics Forum | Mon Mar 13 14:26:45 EST 2006 | Wave Master Larry
Well, im not sure what plane you guys are on, but I can back up my what im talking about. Ya see I wnet to Soltec traingin back in 1995 for our new wave. I got a diploma proofing that I know what i'm talking about. no one else in my company has on
Electronics Forum | Thu Mar 23 22:26:53 EST 2006 | Joseph
Dear all, Referring comment from Mr. Jack,IPC director certification & assembly technology, the term "fillet tearing" is too broad. Cracks or fractures in the required fillet area, with SnPb or LF alloy and whether you call it tearing or not, is a D
Electronics Forum | Wed Apr 05 22:33:57 EDT 2006 | darby
Awww, come on guys, I should never have mentioned beer and fish. Lucky I didn't mention Elle. OK, forget the points and questions 1, (probably correct there Stephen) and 5. Any comments on questions 2, 3 and 4? This bloke's been stranded on an Isla
Electronics Forum | Wed Sep 13 20:04:37 EDT 2006 | mika
Hi, We have a customer that want us to produce a single sided 0.4 x 100 x 50 mm size RoHS pcba approx 1000 of them. The board only contains three 2.54mm pitch Non P.I.P, SMT-connectors. We have never produced such a thin pcb:s before. We are thinkin
Electronics Forum | Sat Dec 09 09:51:14 EST 2006 | pvasquez
Hello Lou, As a high-mix low-to-mid volume manufacturer, you will need to concentrate on equipment that may be progammed very easily, with very quick debug time from assembly to assembly. I have worked with Agilent in the past, and one of my collea