Electronics Forum | Thu Feb 07 12:37:42 EST 2013 | phase1
Resistor/Caps using package library Match-45% White pixel solder-25% search window-25% Tant caps custom teach checking for pattern/value Do you also put a polarity band check in there or just check the value and click the polarity box? same passing
Electronics Forum | Mon May 07 11:09:49 EDT 2007 | davef
4 Fluxer Operation 4.1 Set-Up and Check-Out the Fluxer 4.1.1 Spray Fluxer Set-Up and Check-Out 4.1.1.1 Pass a sample unsoldered board through the machine. 4.1.1.2 Remove the board just after passing through the fluxer and the air knife. 4.1.1.3
Electronics Forum | Thu Jun 04 12:26:30 EDT 1998 | Dave F
| If you could measure and chart 3 variables in my process, what would they be? | The boards that I produce are on panels that are 12up and 2x4 up. All boards are single sided paper base w/o plated thru holes. They are on scored panels that measure
Electronics Forum | Wed May 12 16:31:25 EDT 2004 | Mark @ SolderStar
In answer to your questions. (1) pls can any body throw some light on the reflow profiling? Reflow profiling is the process of confirming that you PCB's that pass through your reflow oven are produced within specifications provided by solder paste
Electronics Forum | Mon Jan 08 10:49:35 EST 2001 | Simon
We are using the omega meters to determine the solvent extract conductivity. The book is refering to standard MIL-P-28809 who specifies a 14 ug/sq. in. of Na/Cl limit. The past owner of our machine was setting the pass/fail limit at 3.6 ug / sq. in.
Electronics Forum | Sun Dec 03 10:05:22 EST 2000 | Steven J
Greetings to all. We are currently experiencing cracking of the ceramic capacitors, on both primary and secondary sides of the PWB. The components range in size from 1206, 1210, to 1815s. The cracks do not appear to alter the electrical properties
Electronics Forum | Mon Nov 20 10:22:18 EST 2000 | Sheng Jin
Hi: Many 75ALS573DW parts we reveived lately from one of our vender have some problem with its pin 2, an output pin of the tranciever ( probably resulting from EOS damage). Its impedance verse GND should be normally 3M ohm up. The parts we have measu
Electronics Forum | Tue Jul 11 11:59:34 EDT 2000 | George English
Looking for some welcome advise again folks. We are currently using a reflow profiling software package which requires passing a data logging unit through the oven attached via thermocouples to a populated 'dummy' PCB. The problem is we have a very
Electronics Forum | Wed Jul 12 13:06:41 EDT 2000 | Brian W.
I have done both. If you have a line that runs both sides in none pass, running the adhesive side first allows you to have one less machine or station for board flipping. If you have to move the board from one line to another, or back to the front
Electronics Forum | Mon Jun 19 14:53:28 EDT 2000 | Mike Demos
I'm looking for some design paramters for perforated tabs. These are the tabs that connect the circuit board to the break-away pannel material. I've never used these before, but I've seen some that have reportedly worked well. These tabs are ident