Electronics Forum: paste and log (Page 1 of 49)

paste Sn42/Bi58 and Lead Finish

Electronics Forum | Fri Nov 02 03:26:40 EDT 2012 | spopov

Hello! We want to try Lead Free paste Sn42/Bi58. Can we use this paste with Lead fihish such as HASL. I am worry about low melting temperature of 138C.

paste Sn42/Bi58 and Lead Finish

Electronics Forum | Wed Nov 14 03:26:38 EST 2012 | spopov

Ryan, in some cases we use 2 pastes with different melting temperature (LF SAC and PbSn)for complex boards with components on two sides. And we want to try to replace LF SAC with low melting paste.

SOT23s and paste + glue

Electronics Forum | Mon Dec 22 11:09:21 EST 2008 | mfcat

We changed paste manufacturers rather recently and are now seeing SOT23s falling off after wave solder. These parts have a dual process... we stencil print paste, apply glue, populate then reflow. Only SOT23s fall off, chips are fine. We do not be

SOT23s and paste + glue

Electronics Forum | Wed Dec 24 20:29:45 EST 2008 | xianhua_tang

Oh,I consider the process is wrong,it is stencil print paste-mount-reflow -apply glue-reflow,then wave solder. it must pass twice reflow,also the first reflow profile is different and the second .

SOT23s and paste + glue

Electronics Forum | Mon Dec 22 12:06:27 EST 2008 | evtimov

Hi, it seems like a glue problem to me. If you don't have enough glue on SOT23, you have no contact and the part is holded only by the paste, which results bad in the waver machine. So first I would check is the glue amount under the SOT. The second

SOT23s and paste + glue

Electronics Forum | Mon Dec 22 14:52:18 EST 2008 | wrongway

We run our process like that all the time paste then glue we use same profile as if we were just reflowing paste once in a while we have A plastic bodied part that has that problem we asume it was some mold relase still on the part basicly comtamena

paste Sn42/Bi58 and Lead Finish

Electronics Forum | Tue Nov 06 22:14:10 EST 2012 | nikyta

Hi Popov, can you tell us the reason for the use of Sn-Bi ?

SOT23s and paste + glue

Electronics Forum | Mon Dec 22 14:15:41 EST 2008 | ck_the_flip

As Emil says, it's 100% the glue! Your paste is not designed to hold parts on at wave solder. Reflow is MUCH hotter than glue, so I doubt you're not adequately heat-curing it. Possibly, the glue cure is "too hot" and maybe making the material brit

paste Sn42/Bi58 and Lead Finish

Electronics Forum | Fri Nov 02 14:46:18 EDT 2012 | ericrr

So how does this (lead free paste Sn42/Bi58) solder compare with the Sn-Ag-Cu (Tin-Silver-Copper) combination which does not flow as well (in the oven), needs higher oven temperature, (that can be adjusted by reducing the oven chain speed) and cost m

copy 'n paste and Netscape

Electronics Forum | Wed Sep 30 10:54:31 EDT 1998 | Clifford Peaslee

Very unusual. It seems to work on some pages, and not on others. I will do some research to try and correct that problem. Cliff

  1 2 3 4 5 6 7 8 9 10 Next

paste and log searches for Companies, Equipment, Machines, Suppliers & Information

Selective Conformal Coating System - GPD SimpleCoat

Easily dispense fine pitch components with ±25µm positioning accuracy.
Selective Soldering Nozzles

MSD Dry Cabinets
Dispenser Pumps

Real Time Process Control BREAKTHROUGH for Dispensing Industry.
Industry 4.0 Reflow Oven

High Precision Fluid Dispensers


High Throughput Reflow Oven