Electronics Forum | Tue Mar 15 07:59:07 EST 2005 | mattkehoe
We are looking for some feedback on this situation. Please let us know if you have any ideas. Thanks in advance. I have been doing some studies on defects and such with our PCB's in prep for lead free and I've come to a conclusion about our process.
Electronics Forum | Wed Jun 24 16:51:25 EDT 2020 | kumarb
Hi. Taking this from a total different angle - why not use ENIG to avoid this issue but find more competitive suppliers? We source from offshore all the time and finding that due to this dreaded virus - the market pricing is soft. Many are willing to
Electronics Forum | Mon Dec 19 08:56:18 EST 2005 | davef
Q1a. If the thickness of the silver is too much (how is too much??), A1a. We have heard stories of using Ag2 to limit silver [or gold] dissolution, but have never seen formal studies to demonstrate that idea. First, exclude the use of silver plate
Electronics Forum | Mon Feb 21 11:34:28 EST 2005 | davef
Assembling boards with 12 pitch are very difficult to control. We like flat surfaces on boards with components below 25 pitch.
Electronics Forum | Tue Feb 22 12:03:32 EST 2005 | russ
You may to reduce a little bit more with HASL. for .4mm pitch and such I would maybe go to a 5 mil with your standards.
Electronics Forum | Mon Feb 21 10:05:33 EST 2005 | Dougs
Our machines can place components down to 16mil, I've never seen any finer pitch components in use, what pitch are they going down to now? 12mil??? What pitches have you been using? We are a contract manufacturer so customers sometimes supply free
Electronics Forum | Tue Feb 22 10:44:12 EST 2005 | Dougs
when you talk about stencil design, what would you recommend for aperture size on fine pitch if the customer insists on hasl finish on fine pitch devices? i usually use a 10% reduction on everything we have been using ( 16mil pitch and upwards and 0
Electronics Forum | Mon Feb 21 18:13:23 EST 2005 | gpaelmo
As davef states above, you would like to have flat surfaces below 25 mil. We are a contract manufacturer also and we've done thousands of 15 mil QFP's with HASL finish with no problems. Your success will depend on quality of PCB supplier providing th
Electronics Forum | Mon Jun 05 14:09:36 EDT 2000 | Jason
We would like to gauge or precentage of production line failures to industry standard AQL level. What would be an acceptale AQL level for assembled pcb's or finished units leaving the factory?
Electronics Forum | Thu Jun 08 02:37:55 EDT 2017 | robertpeng
Carbon ins has very strong resistance to acid and alkali, not easy to remove, maybe return your boards to PCB supplier? they may have solution. Robert Peng- SysPCB
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830