Is it this your first experience of C-CGA RWK ? In order to approach a RWK of this kind of pakage it requires a capable process and clear operating procedure. In the past, the company who I use to work for, we rwkd plenty of this kind of CCGA. Earl
Electronics Forum | Mon Jun 28 11:51:36 EDT 1999 | Brian Wycoff
| | | | Dear guys, | | | | | | | | I have some problem on assembling micro-BGA with solder paste (63/37). The micro-BGA we assmeble is 0.75mm pitch and with 45 pin (solder bump is 96.5/3.5Ag). The stencil is a laser-cut stencil with 5 mil thicknes
Electronics Forum | Fri Jun 25 01:11:31 EDT 1999 | Vinesh Gandhi
| | | Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody
Electronics Forum | Wed May 26 15:56:08 EDT 1999 | Chrys Shea
| | | we have just started wave soldering passive SMT components and through hole. We are having trouble with voids on the SMT components. It is very random, but effects a lot of TSOT's. We are using an electrovert with a chip wave. Are there any
Electronics Forum | Fri Jun 04 14:00:32 EDT 1999 | Arthur Burdick
Wendy, we at ASG make electric presses for press fit connectors, and have made fixtures for AMP Zpak connectors. give me a call i believe we can help. 561-848-6746 Arthur | Wendy.. | | I found that little nugget a good one from my connector supp
Electronics Forum | Mon Apr 01 20:10:24 EST 2002 | davef
Oh. [Howabout if I smack you?] If ahma connectin� wif whut yer sayin�, you: * Don�t like the appearance of the glue slobberin� out from under the component even though there is no apparent glue on solderable surfaces. * Concerned about the hydrosco
Electronics Forum | Tue Aug 31 17:36:36 EDT 2004 | davef
NO-LEAD COMPONENTS WITH LEAD SOLDER ISSUE: We agree with Russ. We've dicussed this several times on SMTnet. For instance, look here http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=25394 LEAD COMPONENTS WITH NO-LEAD SOLDER ISSUE: We disa
Electronics Forum | Mon May 02 12:35:33 EDT 2016 | adamjs
Or try : http://www.sipad.com/ I think sipad is incredibly cool and would be the perfect solution, but is way too expensive. We're paying $0.80/each for four-layer ENIG boards, 50cm^2 with 0.125mm trace/space and 0.8mm-pitch LGA landings in lots of
Electronics Forum | Fri Mar 29 10:11:02 EDT 2019 | cyber_wolf
“For a number of years now, work has been proceeding in order to bring perfection to the crudely conceived idea of a transmission that would not only supply inverse reactive current for use in unilateral phase detractors, but would also be capable of
Electronics Forum | Mon Apr 26 17:45:26 EDT 1999 | Earl Moon
| | | Earl said, in essence: | | | | | | | Justin is absolutely right ... | | | | | | | | Again, Entek is not much more than a flux coating ... | | | | | | | | Metallic coatings protect best, as we all know - especially those electroplated. Those
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830