Electronics Forum | Mon Apr 25 11:24:31 EDT 2005 | Daan Terstegge
I have a question about inspection, touch-up, and how far you need to go to get a product that meets the required IPC-spec. According to some reports (i.e. "New Study Reveals Component Defect Levels" by Stig Oresjo of Agilent) the average defect leve
Electronics Forum | Wed Apr 27 11:43:32 EDT 2005 | patrickbruneel
Hi Daan, What we did in the time was pareto analyses on all board designs to determine the critical areas (mainly design errors) and only inspect those specific problem areas. Every batch had a copy of the PC board with problem areas marked and only
Electronics Forum | Tue Mar 25 08:29:33 EDT 2014 | sara_pcb
Please refer the attached jpegs, The problem is noticed after reflow soldering followed by conventional through hole soldering. Flux used one is MIL Std. Brush cleaning in IPA is followed after each soldering step. regards, R.Saravanan
Electronics Forum | Wed Mar 19 08:38:13 EDT 2014 | davef
I can't picture much of what you're saying, not for nothing, I'm just not connecting. During assembly, solder mask can affected by heat and chemicals. Typically this would be during: * Soldering * Cleaning I will tell you this: Not to defend assem
Electronics Forum | Tue Mar 25 11:43:48 EDT 2014 | sara_pcb
It is Solder Mask on Bare copper, The land finish is HASL as per MIL-PRF-55110G which accepts trace of HASL as acceptable. Wetting is acceptable. regards, R.Saravanan
Electronics Forum | Tue Mar 18 11:53:58 EDT 2014 | sara_pcb
Our contract manufacturing agency have procured pcbs from approved vendor. After assembly we found solder mask separated from the PCB on the epoxy area as patches. The top side is intact. also over the pcb tracks, the mask got damaged. In what c
Electronics Forum | Tue Mar 25 13:55:05 EDT 2014 | horchak
Ok lets put it this way. If the PCB house used a high quality mask and properly applied it to a properly cleaned surface and properly cured it, then as Dave stated above there are only two things that can destroy it. Excessive heat and overly aggress
Electronics Forum | Tue May 15 21:57:06 EDT 2001 | davef
Welcome!!! Where the hay ya been??? Sorry bud, were lining-up with your fab [it hurts me to say that, but when yer ] We used to dry pack with desiccants, also. Its probably an old MIL-STD-2073-1C requirement [er something like that]. We qui
Electronics Forum | Wed May 16 08:48:12 EDT 2001 | ohboy
I been a bunch o' places...! Some good, some bad, re-inventing the wheel in many cases. Our specs are pretty specific in a lot of cases, but that doesn't mean they always get followed. It usually becomes a case of "It's not quite right, but we rea
Electronics Forum | Mon May 21 17:32:23 EDT 2001 | davef
I said: "Our electronic circuit board fabricators seal the boards in moisture barrier bags [MBB]. We discontinued the use of desiccant bags in these MBB because of concerns about the desiccant releasing materials that would affect the solderability
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830
.gif)