Electronics Forum | Sun Feb 11 23:32:43 EST 2007 | M.Haris
1. After reflow some boards start producing bumps/bubbles which damage the internal layers causeing PCBs failed in Electrical-testing. How can I eradicate this problem from my assembling process? 2. If SMT components are mounted on non-rigid FLEX PC
Electronics Forum | Mon Feb 12 11:12:16 EST 2007 | davef
Q1. After reflow some boards start producing bumps/bubbles which damage the internal layers causeing PCBs failed in Electrical-testing. How can I eradicate this problem from my assembling process? A1. Find a proper board supplier. Q2. If SMT compon
Electronics Forum | Thu Aug 29 06:39:29 EDT 2013 | claudiagreene
Many China PCB factories don't have the lamination equipments. Usually,they will send pcbs inner layer finished to other big factory or the lamanation factory to complete this process.It seems it is not what you like. But it is common... Is it ok for
Electronics Forum | Wed Apr 23 19:00:39 EDT 2008 | stevek
It depends on the laminate but a PWB is like any other MSL component. Some fab shops are only waranting standard FR4 laminates for 45-60 days when processed at lead free temperatures. The best thing I can say is to try some weight gain/loss experim
Electronics Forum | Wed Apr 01 04:34:41 EST 1998 | Alan Pestell
We are looking at reflow soldering some Flexi-rigid pcbs. I have heard that IR reflow soldering can make the Polyimide "self heat" and cause de-lamination. Does anyone have any info.
Electronics Forum | Sun Apr 05 09:46:47 EDT 1998 | Earl Moon
| We are looking at reflow soldering some Flexi-rigid | pcbs. I have heard that IR reflow soldering can make the Polyimide "self heat" and cause de-lamination. | Does anyone have any info. The thermal problems associated with polyimide rigid/flex de
Electronics Forum | Wed Jan 28 08:56:40 EST 2009 | blnorman
Don't know the specifics from the IPC spec. However our standard internal spec dictates - highest thermal mass, lowest thermal, most critical component, and center of PCB on the laminate surface. Our profilers have 6 inputs, so the other 2 are dete
Electronics Forum | Wed Dec 13 13:42:57 EST 2000 | Mike Ihm
The dielectic absorption characteristic of printed circuit board materials is usually not listed on the manufacturers spec. sheets. Can anyone point me in a direction to help determine which laminate materials might exhibit better dielectric absorpt
Electronics Forum | Thu Jun 12 03:37:05 EDT 2008 | benefon
It is also possible to etch the barcodes directly on the PCB by using a laser. The solder resist mask is easily burned by laser and if there is copper underneath the contrast is quite good. The contrast is satisfactory even if there is no metal under
Electronics Forum | Fri Jan 24 02:41:58 EST 2020 | borisanic
Thanks Phil. Is there any marks on calibration PCB or it is plain copper laminated PCB with dimensions 20"x20"?
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830
winsouce.jpg)