Electronics Forum | Thu Mar 17 15:34:35 EDT 2011 | grahamcooper22
Dear Rick , thanks for your reply. It is very helpful. I'll get chance to try the Ensolv in a lab next week to see if we can remove the paste residues. Thanks again
Electronics Forum | Fri Apr 27 09:43:04 EDT 2012 | capse
I have worked with Chrys Shea for a number of years. She has written a few white papers on SPI that may be beneficial to you. Here is a link to her website; http://sheaengineeringservices.design.officelive.com/default.aspx
Electronics Forum | Fri May 18 04:04:18 EDT 2012 | vileo72
Dear brotakul , Please let me know if the white paper is traced as the link given is not active . Thanks Vikas
Electronics Forum | Fri May 18 09:58:45 EDT 2012 | capse
Dear brotakul , Please let me know if the white > paper is traced as the link given is not active > . > > Thanks Vikas hello, Chrys recently updated her website; here is the new link http://www.sheaengineering.com/wpapers.html
Electronics Forum | Fri May 18 13:29:10 EDT 2012 | jeremymek
Try here http://www.circuitsassembly.com/cms/component/content/article/159/11751-inspection
Electronics Forum | Mon May 21 11:54:48 EDT 2012 | capse
hi, the link works for me here is the URL for the web site; http://www.sheaengineering.com good luck
Electronics Forum | Mon Mar 26 16:33:54 EDT 2018 | jacobidiego
I realize that I wrote wrong. Sry The stencil of 0,1mm of thickness is printing 45% more volume. I know this becouse the SPI is setup with the stencil gerbers and the messurements have a median of 145% of volume. what do you mean with excesive sold
Electronics Forum | Tue Mar 27 06:27:41 EDT 2018 | cyber_wolf
Occasionally when circuit boards are manufactured, there may be issues with solder mask coverage. It is not uncommon to re-run back through this process to fix missing or thin areas. This can causes the traces to become higher which in turn raises th
Electronics Forum | Mon Dec 06 19:30:23 EST 2021 | duchoang
OSP finish is the big issue here. You almost can not get 100% coverage solder on OSP with 1 over 1 aperture stencil. Reconsider solder coverage requirement in this case. Check your peak temp in profile may help a little.
Electronics Forum | Tue Dec 07 08:01:40 EST 2021 | jineshjpr
Hi DucHoang, Thanks for your response - Understanding that OSP will have more surface resistivity which does not allows the solder to flow on the entire pads. Let me check peak & revert back sooner.