Hi Evtimov, Thanks for your response. Yes, the vapour phase is suppose to handle big and heavy boards, at least thats the intention. Well our thin board is like around 3mm which is not really thin. In our application the thicker the boards means more
Electronics Forum | Fri Oct 10 14:49:21 EDT 2008 | omid_juve
what is the best solder paste type(RA,RMA,R,WS,...) for removing oxidation from the pins of our parts.
Electronics Forum | Tue Oct 14 12:45:32 EDT 2008 | omid_juve
no answer?
Electronics Forum | Tue Oct 14 14:43:46 EDT 2008 | jax
Pump up the Halides.
Electronics Forum | Wed Oct 22 13:10:29 EDT 2008 | shrek
unacceptable statement! Infidel!
Electronics Forum | Wed Oct 22 15:19:07 EDT 2008 | hussman
Not a statement - it's a fact .
Electronics Forum | Thu Aug 28 13:15:59 EDT 2008 | omid_juve
how can i be sure that the device isn`t affected by moisture ? i mean that if the pins are oxidized due to the moisture how can i remove this oxidization ?
Electronics Forum | Sat Aug 30 12:36:05 EDT 2008 | omid_juve
we are doing many experiment on this problem 1)sn63 pb37 solder paste +normal profile 2)sn62 pb36 ag2 solder paste +normal profile 3)pb free solder paste + pb free profile 4)sn63 pb37 solder paste + pb free profile but still the problem exist so i th
Electronics Forum | Wed Sep 23 00:06:34 EDT 2020 | SMTA-64387098
I have modules that come with a 4 x 2 pin header. The problem is the pins must be oxidized as they do not take solder (no wetting occurring). This occurs whether solder in our wave soldering machine or soldered by hand. I tried cleaning the module i
Electronics Forum | Fri Oct 17 14:23:48 EDT 2008 | ratsalad
One of our quality engineers established a procedure to use Tarn-X to clean terminals prior to soldering.