Electronics Forum | Thu Jul 20 16:40:32 EDT 2000 | armintan
Do present reflow and wave solder equipment currently processing tin-lead process need to be replaced when migrating to lead free process ? Is there any equipment (reflow or wave) out there capable of processing both leaded and unleaded processes wh
Electronics Forum | Wed Jan 26 15:38:46 EST 2005 | TomA
Jay, Yes, we did assigned new part numbers for our lead free components. Our concern was how do we know that this component is lead free. New part numbers was our only way. It made the component engineers cry, but offer them a box of Krispy Kreames
Electronics Forum | Thu Jan 20 17:14:39 EST 2005 | jbrower
Today, I have just finished evaluating Kester's EM907 (SAC305)lead free solder paste and found that for our applications it performs as expected. End result that I am encouraged with the results that we got. The equipment that I used: An SMT2020 to
Electronics Forum | Thu Jan 27 15:13:26 EST 2005 | jbrower
Hi Tom, Thanks for the compliment. I've been researching and planning for the time that my company would go lead free since late in 1999. I hear you there, how do we know that the component is lead free. Baring a leap of faith with your vendors, I
Electronics Forum | Fri Sep 22 02:19:25 EDT 2006 | lead free tester
The directive is called RoHS. Meaning that is > not only the lead that is the issue. The > materials need to whithstand a hihger > temperature, not only delta T is an issue (but > huge). Moisture sensitive devices: how to handle > these? You wil
Electronics Forum | Sat Feb 26 22:32:42 EST 2005 | siverts
The directive is called RoHS. Meaning that is not only the lead that is the issue. The materials need to whithstand a hihger temperature, not only delta T is an issue (but huge). Moisture sensitive devices: how to handle these? You will see an increa
Electronics Forum | Mon Mar 29 09:33:37 EST 1999 | Chrys Shea
| I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | What disadvantages are there when using this flux? | Do you have any contact details with
Electronics Forum | Tue Mar 30 08:11:27 EST 1999 | George Steele
| | I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | | What disadvantages are there when using this flux? | | Do you have any contact detail
Electronics Forum | Thu Jan 27 16:43:15 EST 2005 | russ
Ther is a solder alloy out there that is supposed to allow lead free wave processing without having to upgrade pumps and such or increasing the pot temp (direct drop in). I have not used it nor do I plan on doing leadfree wave soldering but you may
Electronics Forum | Mon Apr 05 08:25:31 EDT 1999 | ADRIANO FERNANDES
| | | I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | | | What disadvantages are there when using this flux? | | | Do you have any contact