Electronics Forum: poor smt soldering (Page 1 of 344)

DIMM connector area with poor solderability

Electronics Forum | Tue Nov 22 21:57:17 EST 2016 | Miche

Hello Dears, I'm a small CS Engineering at Taiwan.There are some problem on DIMM connector area with poor solderability at ODM. It was random on Dimm connector area and the SMT area is fine. At the same time, there were other PCB vendor's product whi

ENIG poor wetting

Electronics Forum | Wed Jul 31 17:35:16 EDT 2002 | davef

* Finally, when soldered by hand, do the problem pads take solder? Yes, the XRF analysis will be interesting.

ENIG poor wetting

Electronics Forum | Tue Jul 30 08:37:39 EDT 2002 | davef

When you talk about 'poor wetting', 'dewett', 'no wets', etc.; are you seeing solder pulling back or away from the pad? Please describe the condition. Dewetting. The condition in the solder joint in which the liquid solder has not adhered intimate

Palladium poor wetting

Electronics Forum | Mon May 22 18:19:29 EDT 2006 | Steve

I have read some threads about poor wetting on palladium-silver (Pd-Ag) coated components. I followed the suggestions, but I am still having a problem. The part is an 0603 chip type (Vishay varistor). The Process: solder paste is lead-free Alpha Met

Palladium poor wetting

Electronics Forum | Tue May 23 09:27:37 EDT 2006 | Steve

Sorry I misled you. The PCB pads are wetting, but there is no fillet being formed. After reflow, it looks as though no paste was put down on the pads; however the paste print is fine. All other components solder real nice, it's only the Pd-Ag parts t

ENIG poor wetting

Electronics Forum | Tue Jul 30 17:47:50 EDT 2002 | davef

Dewetting: Solder does not adhere to lead or land, caused by: * Poor solderability of lands. * Poor solderability of leads. * Solder paste integrity. * Lead plating integrity. Need more information, please: * What is dewetting [ie, component, pad, e

ENIG poor wetting

Electronics Forum | Tue Jul 30 12:15:15 EDT 2002 | Rick Lathrop

Hi Dave, The paste applied to the board ends up on the tombstone. The pad has a thin covering of solder most of the time, this is why I think they call it a dewet. Occasionally the pad shows some areas of gold and very rarely are some pads not wet at

Palladium poor wetting

Electronics Forum | Thu May 25 08:00:49 EDT 2006 | davef

The warmest spot you measure on the board is the bare laminate. It will be 10*C hotter than a solder connection.

Palladium poor wetting

Electronics Forum | Tue May 23 09:50:37 EDT 2006 | flipit

They work well in silver conductive epoxy in hybrid applications. They are very poor in no clean applications. They don't work that well in OA solder paste either. Used them once in OA paste and in a nitrogen. They looked just fine. Solder to Pd

ENIG poor wetting

Electronics Forum | Tue Jul 30 17:51:18 EDT 2002 | davef

Comments are: * Peak at 245�C for 40 sec seems like a very long time. I�d expect the time at 245�C to be 10 to 15 sec. This long time at peak could dewett the pads. * Really, their 2D vision on the printer can verify solder presence? * A thin coat

  1 2 3 4 5 6 7 8 9 10 Next

poor smt soldering searches for Companies, Equipment, Machines, Suppliers & Information

KingFei SMT Tech
KingFei SMT Tech

Main Products: 1. Original new and Original Used SMT/AI Spare Parts. 2. SMT Equipments And Related Machine( SMT Calibration, SMT Feeder Carts,Conveyer etc.) 3. Maintenace and Repair Service Pre-Sales Service Provide details ab

Manufacturer's Representative / Manufacturer / Equipment Dealer / Broker / Auctions / Consultant / Service Provider

3 Road Xintang, Fuhai Street,Fuyong
Shenzhen, 30 China

Phone: 13713862102