Electronics Forum | Fri Dec 02 17:28:35 EST 2005 | ratsalad
We have a TCM-V822 over in the warehouse that had a severe head crash. If you suspect you have a bad servopack, contact Unidec. They can test it for you. If it tests bad they can rebuild it for you and you won't have to wait for months to have o
Electronics Forum | Wed Feb 21 14:14:11 EST 2007 | rgduval
Hi, Bill, Lead-free solder and paste manufacturers will be a great resource for you during the transition; they've tested their products extensively, and their application groups have been able to help me through the biggest changes. There are a fe
Electronics Forum | Tue Nov 13 00:05:11 EST 2012 | eadthem
Typical problems with our heller 1707 EXL would be blower issues. We have almost replaced every blower on the top sense purchase. Fortunately Heller is very good about honoring there warranty on the blowers which is quite long, Might be lifetime not
Electronics Forum | Tue Nov 21 22:15:59 EST 2000 | Vince Whipple
Mohammed, The first suggested place to start with your question would probably be with your flux Mfr. Push them! The quantity of dross is effected by several factors: The higher your solder pot temp., the higher your dross level... but don't go too
Electronics Forum | Thu Jul 06 20:46:17 EDT 2000 | Dave F
Mark: An area of increasing interest to all of us. From the SMTnet "Terms & Definitions" (or whatever they call it) Globtop. Encapsulant. Encapsulating. Encapsulation. Potting. Enclosing an article in an envelope of adhesive or encapsulating co
Electronics Forum | Thu Apr 27 21:00:32 EDT 2000 | Dave F
Scott: I�m not familiar with some of the things you�re talking about, but let me: * Agree with Russ & Peter regarding immersion silver. * Give some snips of information on the substrate side of things that might help you to tie this together. � FR-1
Electronics Forum | Mon Apr 17 18:42:32 EDT 2000 | Russ
Murad, I have just completed a switch over in our facility to no-clean. We used Alpha 609 and 857 paste and wave flux respectively. We currently use Alpha UP78 paste, NR330 wave flux, NR205 liquid flux for touchup and cleanline 7000 wire solder as
Electronics Forum | Mon Feb 05 06:57:52 EST 2001 | PeteC
Dason, IPC/EIA J-STD-001C states: "....temperature within the range of 230C (446F) to 290C (554C)." That's a pretty wide process range. 250C has been typical in the past. We run ours from 230C to 240C. We have found that some single-sided PCBs can de
Electronics Forum | Tue Apr 03 22:03:18 EDT 2001 | davef
With friends like you, who needs enemies? I�d guess that the perceived benefits of flat pads for your 20 mil pitch and below components counter-balance the higher cost, gold being a solder pot contaminant, limited solder mask compatibility, potentia
Electronics Forum | Wed May 09 13:11:22 EDT 2001 | zam_bri
Hi.. Recently, I have received a few reels of 0402 with an old date code ( but still less than 2 years old).I don't have a capability in-house to carry out the solderability test except for the dipping test ( dip the components in the molten solder