Electronics Forum | Thu Sep 20 07:18:42 EDT 2018 | proceng1
Has anyone else been experiencing this lately? We have had a rash of boards that come in properly vacuum sealed. We store them in the hot room until we are ready to build, and we get bubbles under the solder mask. We've had 4 different jobs, all di
Electronics Forum | Mon Jan 12 02:56:42 EST 2009 | sachu_70
Hi Bill, You should try pre-baking any such old devices prior to using on SMT Reflow. Refering to MSL-type3 guidelines could help in your case.
Electronics Forum | Fri Jan 07 07:36:14 EST 2005 | dansmall
I have a Polyimide board that is showing signs of de-lamination. I was wondering what pre-bake times and temperatures other people would recomend for new boards as well for boards that have been on the shelf for 8 months.
Electronics Forum | Wed Jan 12 10:05:20 EST 2005 | Dreamsniper
we are using polyimide boards 6 inches x 7 inches, 2.5mm thick, 12 to 14 layers, for aerospace industries. I am using a long bake of 12 hours at 70'C prior to manufacturing or exposure to elevated reflow and wave soldering temperature. If schedule i
Electronics Forum | Sat Jan 08 08:50:35 EST 2005 | davef
Normally, you should not have to bake boards that are properly packaged and stored. Since you are seeing problems, baking makes sense. Consider 125C for 4 to 6 hours. Additionally, look here for more, while waiting for others: http://www.smtnet.
Electronics Forum | Thu Oct 17 05:16:44 EDT 2013 | vincentdesilva2003
Anyone can help me how many percentage of blowholes and pinholes if i do the followings: 1. Increase copper plating thickness more than 25 microns. 2. Pre Baking of PCB to remove gassing by drying out the PCB's
Electronics Forum | Thu Jun 24 11:41:10 EDT 1999 | John Thorup
| Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody hel
Electronics Forum | Fri Jun 25 01:11:31 EDT 1999 | Vinesh Gandhi
| | | Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody
Electronics Forum | Thu Jun 24 12:43:08 EDT 1999 | Earl Moon
| | Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody h
| 1 |