| Can anyone pls email me a typical temperature profile for wave soldering process. | | Thank you vey much. | | rdgs... | Typical depends on the processes you're developing. Key factors in my experience are flux type and requirements, component
Electronics Forum | Tue Apr 27 12:14:08 EDT 1999 | M Cox
Board Experts I am fighting with a board house about a delamination problem.. First the facts 1) 10 layer board .063 thick HASL Finish Aprox 16 in x 17 in. 2) 150 Boards with this part number built with the same reflow oven settings (212 c max t
Electronics Forum | Tue Apr 27 09:31:45 EDT 1999 | Robert L. McCallum
On circuit board assemblies first pass yields need to be above 98%, if a supplier is below this level it is a indication that: he has poor control of the manufacturing process; Poor component selection (price over quality; excepted a poor design from
Electronics Forum | Thu Apr 22 13:20:04 EDT 1999 | Ben Kirk
| On various PCB's after building processes,such as reflow, flowsolder and wash. The soldermask on the PCB's have become discoloured, like a 'marble' effect all along the solder side of the board, it is lighter in contrast than normal, although when
Electronics Forum | Thu Apr 22 14:36:33 EDT 1999 | Dave F
| On various PCB's after building processes,such as reflow, flowsolder and wash. The soldermask on the PCB's have become discoloured, like a 'marble' effect all along the solder side of the board, it is lighter in contrast than normal, although when
Electronics Forum | Thu Apr 22 18:07:38 EDT 1999 | Tom B.
| On various PCB's after building processes,such as reflow, flowsolder and wash. The soldermask on the PCB's have become discoloured, like a 'marble' effect all along the solder side of the board, it is lighter in contrast than normal, although when
Electronics Forum | Mon Apr 26 11:04:53 EDT 1999 | Dave F
| | Earl said, in essence: | | | | | Justin is absolutely right ... | | | | | | Again, Entek is not much more than a flux coating ... | | | | | | Metallic coatings protect best, as we all know - especially those electroplated. Those coatings chemi
Electronics Forum | Mon Apr 19 22:52:59 EDT 1999 | Dean
25 PPM)! | | 1. Is there a better process to solder the leads of QFP's with lifted "minute" lifted leads still having a realiable solder joints? | | 2. Or has anybody tried modifying solder pads and use thicker solder paste deposit to compensate fo
Electronics Forum | Tue Apr 20 23:18:48 EDT 1999 | KEVIN SIMPSON
25 PPM)! | | 1. Is there a better process to solder the leads of QFP's with lifted "minute" lifted leads still having a realiable solder joints? | | 2. Or has anybody tried modifying solder pads and use thicker solder paste deposit to compensate fo
Electronics Forum | Tue Apr 06 09:50:58 EDT 1999 | Justin Medernach
| Does anybody put QFP's on the backsides of boards? Can they be reflowed without falling off? Do you use adhesive? | I use a double sided reflow process all day, everyday. I've hung QFP240s with embedded heat sinks and they don't fall off. Yei