Electronics Forum | Mon Mar 06 10:59:42 EST 2006 | ezamborsky
Sorry to hear of your problems with your VPI-1000. As most people know the VPI line was transfered over to the Easy Braid Company last July. With most changes of this type there can be some initial confusion and and unneccessary stress placed on endu
Electronics Forum | Tue Aug 30 09:18:40 EDT 2005 | PWH
Agreed - D.I. a must. Also, operators will have to pay attention to lesser stencil life than no-clean paste. Product specs. might say the stencil life is similar but experience has showed us that no-clean last much longer and rolls for a longer tim
Electronics Forum | Thu Sep 01 18:27:28 EDT 2005 | Board House
Hi I currently Manufacture product for Dataradio Inc. in Quebec. and would be interested in quoting your product. We are a Multi-layer facility in Minnesota, we currenty manufacture layer counts between 2 & 18 layers. Line widths and Spacing down t
Electronics Forum | Fri Jun 23 12:17:11 EDT 2006 | kevindebarra
Dear Greg and PWH, I see from your comments above, that you are still unsure whether splicing is for you, and mention that you have yet to find a "good splice tool." QTEK Manufacturing Ltd. based in Ireland, Mexico and Hungary provide a unique tool
Electronics Forum | Thu Nov 10 21:15:39 EST 2005 | davef
Years ago, there was discussion of making a "IPC-A-640" to define requirements for assemblies comprised of more than a circuit board assembly. We don't know what happened after that. As an alternative consider: Telcordia GR-78 - Generic Requiremen
Electronics Forum | Wed Nov 16 08:56:17 EST 2005 | mskler
Hello every one, I will be very thank full to all who are using CP6 fuji machine if they can spare some time for me & give some important information about the machine. 1.What is the actual CPH you are getting during production. 2. W
Electronics Forum | Thu Jan 12 13:39:14 EST 2006 | sarar
If you want to try and reduce the dross, there is a really interesting product out there that you might want to examine called MS2 - it's developed by P Kay metals out in LA, and is known to completely eliminate dross in lead free processes. I'm not
Electronics Forum | Wed Feb 01 03:38:56 EST 2006 | Jose Luis
Hi all, I'm working in Military Production and then, We have an exception about RoHS (LEAD FREE), but, because we use "normal" components, in this moments, a lot of components have LEAD FREE terminations, and we think that after of 1st July, we wo'nt
Electronics Forum | Tue Jan 31 17:14:51 EST 2006 | Chris
I would not go by any general rules at all. Test the product! Thermal cycle it and shock and vib test it. Got burned on a part that had 0.010" dia bumps. Manufacturer stated undefill was not necessary on their part due to bump size. I wanted to u
Electronics Forum | Thu Mar 09 16:14:19 EST 2006 | marc
CGO Assuming your system is performing well here are a few ideas to help out your profile.... - Pull the material spec and ensure you are meeting the requirements for times and temp. Many times the material will allow a mild soak of the board prior