Electronics Forum | Wed Jul 21 01:52:40 EDT 1999 | Scott McKee
| Dear all | Please help me to know what kind of tests usually done after SMT Pick & place and reflow oven. | Our appliocation is Mainly fabrication of mother boards. | Thanks | In theory, ICT is the classical answer (In-Circuit Test). In practic
Electronics Forum | Thu Jul 29 01:01:11 EDT 1999 | DLKearns
| Dear all | Please help me to know what kind of tests usually done after SMT Pick & place and reflow oven. | Our appliocation is Mainly fabrication of mother boards. | Thanks | Hunter, YES ICT after SMT reflow is expensive, we currently onlt t
Electronics Forum | Tue Jul 20 11:33:55 EDT 1999 | Ted Kress
| | I'm planning to introduce selective point-to-point soldering for pwb. This is due to various needs: PIHs assy on double IR, for example. I think the most suitable solution is a point-to-point soldering, 'cause we're still having small lot/many ty
Electronics Forum | Thu Jul 15 21:10:53 EDT 1999 | Scott McKee
| I was wondering if someone could help me with a little problem I am Having with a MyData TP-11 UFP running TPSys 1.4.2. Early this week the machine crashed and I had to reload the software. I re-insatalled Venix then the CP4 driver then TPsys and S
Electronics Forum | Fri Jul 16 05:48:06 EDT 1999 | Wayne Sanita
Give Mydata a call as Scott said, they will take step by step over the phone. Wayne | | I was wondering if someone could help me with a little problem I am Having with a MyData TP-11 UFP running TPSys 1.4.2. Early this week the machine crashed an
Electronics Forum | Tue Jul 06 10:12:44 EDT 1999 | John Thorup
| | Is the no clean solder paste as good? We are wondering if we can elliminate the wash when we change from through hole to surface mount. | | | John, | | No clean is as good as your process, and the paste you are using. Everything I do is no cle
Electronics Forum | Mon Jul 05 02:32:14 EDT 1999 | Vinesh Gandhi
Dear All, We are a medium sized Electronic manufacturing company manufacturing computer motherboards and Telecommunication products. We have a big debate going on within our company regarding the defect rate measurement technique. At present we
Electronics Forum | Sat Jul 03 18:45:19 EDT 1999 | Scott Cook
| John, | | You said a bunch. My biggest problem running Fuji, Panasonic, or Sanyo high speed stuff is that they are meant to run free. They are meant, in my mind, to run as thoroughbreds. | | I watch 6" reels placed on feeders, placed on the carts
Electronics Forum | Sat Jul 10 12:57:15 EDT 1999 | Steve
| | John, | | | | You said a bunch. My biggest problem running Fuji, Panasonic, or Sanyo high speed stuff is that they are meant to run free. They are meant, in my mind, to run as thoroughbreds. | | | | I watch 6" reels placed on feeders, placed on
Electronics Forum | Thu Jul 01 14:47:10 EDT 1999 | Tony
| | | My guess would be trapped flux continuing to be active after soldering. Is the tarnish there immediately after exiting the machine? Do you remove the mask and wash right away? If the solder is reflowing under the mask on the component side