Electronics Forum | Wed Sep 01 13:51:38 EDT 1999 | Dave F
| Planning to evaluate the above process... | Can anyone can give me some tips/infos on the above.... | e.g. stencil aperture design, aperture ratio, common problems and solutions they encountered on the above process, is the profile different from a
Electronics Forum | Fri Aug 20 17:17:14 EDT 1999 | K.T
| | | | Yesterday as I was creating a profile on a plastic BGA using Conceptronics freedom 2000 rework station, I happend to discover that I was able to remove solder bridging from a plastic BGA. | | | | | | | | This is what I did. | | | | | | | |
Electronics Forum | Fri Jul 16 22:44:27 EDT 1999 | Vic Lau
| We are currently assemblying several different board type with gold plated lands with varying results. Can any of you that has successful experience in this area give me some pointers. What paste do you use? Do you use the recommended reflow pro
Electronics Forum | Wed Jul 14 09:33:18 EDT 1999 | Dave F
| Our plant in Slowakia tries to convince me that it is not possible to reflow FR2 PCB-material. | At this moment the PCB's leave the reflow dark coloured and they are schrinked. | | I'm still waiting for a reflow profile, because I can't believe th
Electronics Forum | Thu Jun 24 04:38:31 EDT 1999 | Vinesh Gandhi
Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody help
Electronics Forum | Mon Jun 14 11:44:10 EDT 1999 | Vince Gedgaudas
Has anyone had issues where bottomside double reflowed smt has fallen off in the wave when using voc-free flux? I have verified the hotter profile was not the issue by using an alcohol based flux with no problems.This voc-free flux is also not causin
Electronics Forum | Mon Jun 14 07:23:42 EDT 1999 | Vinesh Gandhi
We are a medium sized PCB assy. house manufacturing about 2000 motherboards a day. There is a major problem we are facing at the wave soldering stage, i.e. warpage of the PCB. As soon as the PCB touches the wave it warps severely from the centre to
Electronics Forum | Wed Jun 09 14:51:08 EDT 1999 | Earl Moon
| Does anyone have thoughts on BGA rework. We now use the OK BGA 3000 and now am considering an Infrared machine. Any thoughts? | I've used Pace, Conceptronic and, now, SRT machines. Bottom side IR is OK. Better thermal balance is achieved with hot
Electronics Forum | Tue Jun 01 08:30:51 EDT 1999 | Dave F
| I have difficulty to convince my management to air-condition our manufacturing facilities. The room temperature fluxuates from 8 deg.C in the morning to 25 deg. C in the afternoon. The PCB topside temperatures in the reflow oven and wave soldering
Electronics Forum | Thu Jun 03 18:53:27 EDT 1999 | Raeto Zryd
| | I have difficulty to convince my management to air-condition our manufacturing facilities. The room temperature fluxuates from 8 deg.C in the morning to 25 deg. C in the afternoon. The PCB topside temperatures in the reflow oven and wave solderin