Electronics Forum | Mon Apr 19 20:49:13 EDT 1999 | Dave F
| Netters, | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | 1. Kester 293 no clean | 2. 2.1 C/s for 30s to 150 C | 3. .5 - .7 C/s for 60s to 185
Electronics Forum | Tue Mar 23 10:16:22 EST 1999 | Chrys Shea
| Hi Folks, | This is my first surface mount board, so I asked our assembly house for some tips. They said only passives on the bottom side-preferably no smaller than 0805, 0603 only if I have to. I would think that an SOT-23 would be OK on the botto
Electronics Forum | Tue Mar 16 19:25:32 EST 1999 | Earl Moon
| | Looking for a company that makes a small batch reflow oven. Not a belt-style convection oven, but a cabinet style that can 125 c to 150 c. | | | | Thank you | | | TRY GE I HAVE ONE AT HOME THAT COOKES PRETY DARN GOOD. And it will get hotter if
Electronics Forum | Tue Mar 16 20:09:01 EST 1999 | Wayne Bracy
| | | Looking for a company that makes a small batch reflow oven. Not a belt-style convection oven, but a cabinet style that can 125 c to 150 c. | | | | | | Thank you | | | | | TRY GE I HAVE ONE AT HOME THAT COOKES PRETY DARN GOOD. And it will get
Electronics Forum | Wed Mar 17 17:14:49 EST 1999 | Michael Allen
Another test to consider is dye penetrant analysis. The technique involves flooding the area beneath the soldered part with dye (preferably a bright color, like red). After drying the board+dye in an oven, you peel or torque the part off and inspec
Electronics Forum | Sat Mar 06 08:01:45 EST 1999 | Scott Cook
| Can someone please advise me to the rework procedure for removal and replacing Ceramic Chip Capacitors (e.g. 0805, 1206, etc.)? | | Is it necessary to pre-heat ceramic capacitors before soldering them onto a PCB with a soldering iron? Is this just
Electronics Forum | Mon Mar 01 12:50:47 EST 1999 | justin medernach
| Hello! SMT professionals, | | I do not know if anyone posted this question before. | Last week, I reflowed our newly designed thin Rigid-Flex pcb with 0.040" thickness. I found all of pins of a TQFP48 ic did not get wetted. I could see on the hee
Electronics Forum | Mon Mar 01 22:37:01 EST 1999 | Dave F
| Hello! SMT professionals, | | I do not know if anyone posted this question before. | Last week, I reflowed our newly designed thin Rigid-Flex pcb with 0.040" thickness. I found all of pins of a TQFP48 ic did not get wetted. I could see on the hee
Electronics Forum | Tue Jan 12 14:59:14 EST 1999 | Earl Moon
| What would be a good metric for process control of a stencil printer? (fully automatic, vision equipped, stendil printer). | I'm doing some more DEK 265 GSX's with everything imaginable hung on them. Have done Lt's and the MPM2000. This makes mach
Electronics Forum | Wed Dec 02 21:58:19 EST 1998 | Dave F
| | I am looking for a few PBGA 560 1.27 pitch Components. If anybody has any lying around I could buy. So that I may profile to my hearts content. | Thanks | Mike Cox | Mike: The best I can offer is contacts at dummy component suppliers, wh