Electronics Forum | Wed Oct 04 14:14:49 EDT 2006 | russ
Change mfgrs of paste OR better yet use pbfree paste, If you are collapsing the balls on the BGA then you are possibly overheating the paste/flux quite a bit. most lead pastes do not like much more than 230 C. I am assuming that you have a decent p
Electronics Forum | Tue May 20 06:00:33 EDT 2008 | roc2x
Im qualifying a new PCB. I run 2 diff supplier. Supplier A has Zero failure. Supplier B has 4 failure all having Lifted PAD on Bga same location and same location pads that lifted. How can I prove that the PCB have problem? Input : Both run in same o
Electronics Forum | Fri Dec 07 06:05:58 EST 2018 | cyber_wolf
63/37 goes from solid to liquid. It melts and solidifies at a single temperature. You can add a percentage of silver and get a slight "pasty range" for a couple seconds. I have never seen a temperature change in a profile keep this from happening w
Electronics Forum | Mon Jun 10 13:47:23 EDT 2019 | don_julio
First thing we did was visit the profile and we have it adjusted as far as we're willing to take it. I'm just going to make a carrier design in cad and have the board house produce some in their thickest substrate to see how it works out. Thanks.
Electronics Forum | Thu Mar 13 01:42:58 EDT 2008 | Sean
Thanks Real Chunks and Davef...Yours input is valuable to me. My inputs towards your question asked below: Questions are: * Why did you tell us the following? "This BGA is installed with heatsink (with hook at both side of the heat sink) manually b
Electronics Forum | Tue Oct 22 17:23:35 EDT 2002 | Yannick
Hi, I wondering if someone know the anwser to that. I'm using a solder paste 63/37 and on the solder joint we have a tiny little layer or flux who is like crystalin. I try to play with my profile the get it off but I don't get much success. So D
Electronics Forum | Thu Jul 14 10:41:27 EDT 2005 | slthomas
I guess I took too much time editing my response. :P The bottom line is that unless you're measurements are at least as repeatable and accurate as your machine's closed loop systems, it's a waste of paper *BUT* makes nice wall art for tours. I like
Electronics Forum | Thu Jul 14 11:04:53 EDT 2005 | dougs
yes SPC can be used on a wave solder machine, you should use a c-chart to monitor the amount of defects per board or group of boards, this will let you know if your process is stable, as you improve your process you should re-calculate your UCL, hope
Electronics Forum | Sat Dec 16 08:23:11 EST 2006 | pr
The "Wave optimizer" is a little pricey but is easy to use, gives instant feedback (display on the unit as opposed to hooking it up to a computer)and will give feedback on the waves, as well as preheat. They will send you a unit to trial for a week o
Electronics Forum | Mon Dec 18 13:00:47 EST 2006 | grantp
Hi, We have a white residue, which is visible, and we would like to have the produce clean as it's a PCI card, so users see the PCB. I am wondering if we need to install a cleaning stage to the line for these kinds of products. Can anyone give som