Electronics Forum | Fri May 14 17:06:29 EDT 1999 | Ryan Jennens
| | Hi Guys, | | | | I am going to be graced with the good luck of processing microBGA's in the near future. A bit of a step forward from printing 20-mil pitch and wave soldering 0805's, wouldn't you say? | | | | So, any of you folks who have alre
Electronics Forum | Tue May 11 00:47:59 EDT 1999 | P.L. Sorenson - Technical Consultant
| | | | | | | I left the company before this thing ever got resolved, so I don't know the answer, but here's what we did to get boards out the door. Baked them in a desicating oven. You know, the kind that pulls vacuum? It was a regular overnigh
Electronics Forum | Tue May 11 06:30:41 EDT 1999 | Joe Byrde
| | | | | | | | | | | I left the company before this thing ever got resolved, so I don't know the answer, but here's what we did to get boards out the door. Baked them in a desicating oven. You know, the kind that pulls vacuum? It was a regular
Electronics Forum | Sun May 16 13:10:36 EDT 1999 | Dave McDermid
| | | | | | | I left the company before this thing ever got resolved, so I don't know the answer, but here's what we did to get boards out the door. Baked them in a desicating oven. You know, the kind that pulls vacuum? It was a regular overnigh
Electronics Forum | Tue Apr 27 16:44:05 EDT 1999 | Chrys Shea
| | Has anybody had experience wavesoldering 1 watt 2512 resistor packages?? I know it can be done, but are there reliability issues? | | | | We are in the middle of a new product and the question was posed to me "Can we use 2512 1 watt resistors o
Electronics Forum | Thu Mar 11 09:50:34 EST 1999 | Scott Cook
Hi Steve. glad your equipment will be back on-line soon. Takes a load off, doesn't it? I'd like to respond to the following comment: | "YOU'VE PAID A LOT OF MONEY FOR YOUR EQUIPMENT, YOU'VE GOT TO TAKE CARE OF IT ON A REGULAR BASIS!" | | What c
Electronics Forum | Tue Jan 12 09:29:37 EST 1999 | Dave F
| | | We are currently fighting a dross battle on our non-inerted waves. We are currently using a bar solder that barely meets QQS-571 for Alloy/Impurity. | | | | | | Is anybody using HI FLO in a non inerted wave? Do you see a measureable decrease
Electronics Forum | Tue Sep 15 19:54:13 EDT 1998 | Wayne Bracy
| Dear Dynapace and those who responded: | Sorry we were not quick enough to delete this ad. However, this gives us a chance to discuss with both users and vendors on ways to facilatate the desemination of product informtion other than via the Forum
Electronics Forum | Tue Jun 09 07:35:23 EDT 1998 | Steve Gregory
Hi there Gary, Your solder ball problem is very similar the problem I experienced, but I was using a water soluble paste at the time. It started by inspectors telling me that they were seeing cold solder on some SIMM's that we had built regularly. W
Electronics Forum | Tue May 26 15:49:05 EDT 1998 | Earl Moon
| | We currently bake plastic SMT parts in accordance with the IPC guidelines for moisture sensitive parts. Because we have double-sided boards that are subjected to either an aqueous or semi-aqueous cleaning process, we do a 24 hour bake at 125 deg