Electronics Forum | Mon Mar 31 11:10:43 EST 2003 | davef
First, most �thermal shock� recipes are not a reliability test. There is no relationship between the failures seem in these tests and in-use application. These tests show you the failures in these tests. That�s it!!! Second, accelerated life test
Electronics Forum | Fri Apr 11 09:36:55 EDT 2003 | davef
We don't know anything about using "old Tango for DOS". First, consider the fabricator of your part as the THE most appropriate place to look for layout recommendations. We've discussed the heirarchy of sources for layout information previously he
Electronics Forum | Thu Apr 17 17:38:57 EDT 2003 | Takfire
Dave, I am not exactly sure what is driving them to believe that this is a capacitor issue. It is unfortunate, that this belief has slowed their activity in further understanding their manufacturing process. The caps are BME (Base Metal Electrode
Electronics Forum | Wed Apr 30 14:35:35 EDT 2003 | clarkk
Hello all, We have received reports from two customers about electrical leakage on pcb assemblies that used Kester paste #HM531 (63/37) and washed with Kester 'Bio-kleen' saponifier and DI water. The leakage is such that when the boards receive power
Electronics Forum | Thu Jul 03 03:23:04 EDT 2003 | loz
I have been advised recently about pcb manufacturers, that somehow or other supply pcb's with contamination. Visually they are fine, but problems arise during SMT manufacture, ie solder balling, non-wetting on pads, and also during wave solder proces
Electronics Forum | Fri Feb 20 08:56:42 EST 2004 | davef
We successfully clean WS flux on 1mm and 1.25mm pitch BGA. For 0.8mm pitch BGA, we use no clean, because we cannot remove the flux residue from under them efficiently. Use ion chromatography testing to be sure it is clean under the BGA. IC is the on
Electronics Forum | Thu Mar 25 15:01:45 EST 2004 | patrickbruneel
Why are you guys not simply switching to No-Residue?? Residue free soldering is not a dream, it is a reality and is succesfully implemented for over a decade. I am the founder of no-residue technology, a technology developed to effectively compete w
Electronics Forum | Fri Apr 30 10:56:27 EDT 2004 | Bryan She
We tested J6 open on .5mm pitch CSP(In fact,only resistance much lower than normal).J6 is one of the corner ball of the CSP.Defect rate is about 3%. Stencil:4 mil thickness,10 mil square aperture, solder mask openning:10 mil diameter circle. Board fi
Electronics Forum | Mon Jun 14 11:00:50 EDT 2004 | raylawre
This is one reason why we changed package styles. Maybe consider getting a different size tube, say from 500g to 1000g or something like that. We use jars for lead paste, and tubes for lead free (different application method) If lead free comes off t
Electronics Forum | Wed Jul 28 18:51:52 EDT 2004 | gregoryyork
Found problem many years ago by chemical extraction and IR analysis, produces alarming amounts of plasticizer from under cured or incorrect mix of hardener to liquid photoimageable solder resist. Problems this causes are endless and many things blame