SAC 305 Reflow & SN100C Wave and Selective

Electronics Forum | Thu Feb 15 10:48:34 EST 2007 | ck_the_flip

Is there anybody out there doing this scenario: SAC 305 Reflow & SN100C Wave and Selective Can the 2 alloys be mixed on 1 board, say, SAC 305 for SMT, and SN100C for thru-hole? Are 2 different rework chemistries needed, or can one use SN100c wire

SN100C vs. SAC 305 wave soldering

Electronics Forum | Fri Mar 03 13:44:36 EST 2006 | Jon Provost

We switched to Sn100C on 2 waves and kept one with SAC305. The SAC305 will be converted to SN100C as soon as the Aim rep. delivers it next week.

Mixed SAC105 and SAC305

Electronics Forum | Thu May 29 13:12:10 EDT 2008 | yam6rider

Just like to know what you guys thoughts regarding mixed alloys. Production run SAC305 and some components are SAC105. So, which profile should you follow. SAC105? or SAC305.

Using SAC 305 Solder

Electronics Forum | Wed Sep 28 03:58:05 EDT 2011 | Jacki

Hi All My company is doing PCB assembly.To save cost, we change our wave solder bath from SnAg to SAC 305. What is the pros and cons for using SAC 305 solder? And,will affect to our quailty? Thanks in advance.

SAC305 Lead Frame Component with Leaded Process?

Electronics Forum | Tue Sep 16 09:25:49 EDT 2008 | trynders

I had a vendor change thier lead finish from tin/lead to a SAC305. We built up several assemblies before we realized the change. The reflow process is a standard leaded profile peaking at 220 C. What are the reliablity concerns with mixing the tin/l

Steps to Convert SAC305 Wave Solder Pot to SN100C

Electronics Forum | Mon Sep 29 21:32:52 EDT 2008 | bobsavenger

I was wondering if someone could tell me the steps they went through to convert a SAC305 Wave Solder pot over to SN100C. I'm having wave solder problems with SAC305 and I'm considering a change to SN100C. Didn't know if it was a -in replacement or

SAC305 and Sn100c alloys

Electronics Forum | Thu Jan 29 17:04:43 EST 2009 | jeffjarmato

I run two different waves here one with SAC305 with aqueous flux the other with SN100C and No clean flux. Does anyone see any issues with running product through either machine of course after changing the Flux type? I also only use SAC305 alloy for

choices for SN100C for reflow

Electronics Forum | Mon Jan 23 19:48:27 EST 2012 | gaz

This make me curious how many people are using sn100 versus how many using sac305. The sn100 seemed to generally cover the pads and flow a little better, and looked nicer, but SAC305 overall was easier. Is this normal or do I need to work more on sa

Lead Free Dross

Electronics Forum | Wed Jan 11 16:27:36 EST 2006 | cg

SAC305

Tombstones? Pb vs Pb Free

Electronics Forum | Tue May 09 14:23:40 EDT 2006 | flipit

I would like to know what you are seeing in production. I have read the papers that state fewer tombstones with SAC305 as well as the papers that state more tombstones with SAC305. I am seeing more tombstones with SAC305. I place a lot of 0402 com