Electronics Forum | Tue Jul 08 12:11:17 EDT 2008 | gabriella
Hello, you will probably need more temperature. Notebook - probably the board is designed to transfer more heat(insude layers all copper). Tell us more about the problem you have and something about the board. what exactly is your problem? You can't
Electronics Forum | Fri Jul 18 16:02:25 EDT 2008 | wrongway
I think Real Chunks has your answer home plat or reverse home plate or like we use a 10% reduction on most aptures vs pad I think your problem is to much paste on the pads we used to see a lot of that with 8mil stencil thicknes on our 1206 caps went
Electronics Forum | Mon Jul 28 13:16:47 EDT 2008 | realchunks
Be careful of just reducing your aps. Too much can cause tombstoning if your print is slightly off or your placement isn't right on. Also be careful of the "pac-man" type of ap - it can lean to asty cuts if you wipe off your stencils by hand. Do
Electronics Forum | Thu Jul 31 07:28:04 EDT 2008 | leemeyer
This sounds like a Quadalign problem. Upon startup the Quadalign system checks runout of the Z-rod and tries to find the tip of the nozzle. It will keep lowering the Z-rod and looking for the tip until it hits it's limit. Check and see if the Quadali
Electronics Forum | Mon Aug 11 15:44:41 EDT 2008 | stimpk
Although its a fairly rough image to look at I'd think you more of a reflow or paste issue. Looking at the two resistors, they don't look so good either. Although they maintained their placement alignment the solder does'nt appear to have flowed cor
Electronics Forum | Mon Aug 11 11:13:05 EDT 2008 | davef
So, how did you get some parts going one way and other parts going another way? It would be highly unusual to receive a reel packaged that way. No, don't send the data sheet. We can see that Vcc is on pin 8 of the part. What pin of this component do
Electronics Forum | Wed Aug 27 11:09:55 EDT 2008 | fede
I�m interested in the F1 model, due to the possibility of this system to be configured with 1 top camera and 4 side. We are manufacturing 0402 and 0.4mm fine pitch Lead Free, and our PCB�s quality is not very good. With just one camera are you able t
Electronics Forum | Thu Aug 21 08:33:09 EDT 2008 | davef
There is no standard as such. It's easy to see why. It's too complicated and has such a small payoff. Standoff is comprised of: * Package height * Solder thickness between the pad and the component lead * Delta of pad thickness and solder mask For p
Electronics Forum | Tue Sep 09 19:35:26 EDT 2008 | vladig
OK. Here it goes. It's a series images taken after cross-sectionning one of the components. I hope that it's obvious now that teh "knob turning" technique wouldn't work that time around :-) I have one more image in my "back pocket", which explains
Electronics Forum | Tue Sep 02 22:08:34 EDT 2008 | davef
MacDermid Sterling seems to take-on a brownish tint in high dew points. Look at figure 3, p14 here: http://www.enthone.com/docs/CircuiTreeNov2006ImAgStudy.pdf We not so sure that it's fatal. That you see Cu makes us nervous. Since your XRF is doin