Electronics Forum | Fri Feb 01 06:15:46 EST 2002 | nifhail
This can be a solution for IC/BGA soldering for lead-free process isn't it ? See, most of the reflow profile set meets solder paste specification but often violating ICs or BGA requirement. Most of the solder paste required temperature of about 205 -
Electronics Forum | Mon Feb 18 17:27:03 EST 2002 | hgwells
Agilent has a great article on determining whether automated optical inspection (AOI) or automated x-ray inspection (AXI) is right for you. It's a PDF file that can found here: http://www.ate.agilent.com/EMT/LIBRARY/X-RAY/DOCS/59883661en.pdf To sum
Electronics Forum | Thu Feb 21 10:13:27 EST 2002 | Vince Whipple
Hi Dave G, This is an interesting problem.. I can only add the following: - Try trimming the pins and see it this helps.. sometimes the decreased surface area will lessen the surface tension enough to minimize the effect of bridging. - As Dave F was
Electronics Forum | Thu Mar 21 00:01:46 EST 2002 | jbutile
Can anyone give me a good reason to stay in this industry. I really do not want to be the last one in this forum while I see all my friends move on to other jobs, reasonable pay and security. From all I can tell it is over, there is nothing left to
Electronics Forum | Wed Mar 27 11:30:20 EST 2002 | itempea
Just a question: have you ever tried to transfer programs between 2 identical MPM printers, or between 2 identical CAMALOT Geminis? Well, you'll be surprised to find out that you have to spend 15 to 30 min tweaking them on the second machine. And th
Electronics Forum | Wed Apr 03 13:32:30 EST 2002 | Bob
Hi, Just to ease your mind a little. I have 15 years experiance on Fuji kit, and was the engineer in charge of over 30 CP6's. They are very robust and the electrical / electronic side is pretty bomb proof. The main thing to look out for is wear in
Electronics Forum | Mon Apr 01 07:41:40 EST 2002 | davef
Hey Bob, Boy, you are lucky to have a laboratory, and now colorful pix!!! The only silver IMC that you will see are: * Ag6Sn, much less likely at 'normal' soldering temperatures * Ag3Sn, much more likely Allowable silver concentration: * Below 2%
Electronics Forum | Sun Apr 28 07:34:34 EDT 2002 | hany_khoga
Dear Tom : I hope I �m not too late. We produce PC motherboards with some buses exceeding the speed of 100MHz . we use no clean flux and it is OK even with the residues you can see under a microscope. But according to our own experience through a mo
Electronics Forum | Tue Apr 23 13:51:03 EDT 2002 | Ken Bliss
We get inspected regularly and the only items we have had to ground where flammable liquid drums or a drum that had flammable or explosives fumes (partially full), I cannot see any reason why they would require grounding if no hazard was present. We
Electronics Forum | Thu May 22 11:25:35 EDT 2003 | nad
Hi Jon, I recently had the opportunity to look over a used IIIc converted to a IVc. The documentation, software and spare parts supplied with the machine seem more than adequate, however, upon spending several hours cleaning, oiling, familiarizing,