Electronics Forum | Tue Sep 17 15:40:59 EDT 2013 | 18424
Good day all, I wanted to get a quick poll from the folks running SAC305 in their selective soldering equipment. How are final results? How repeatable is the process, any machine related failures? pumps? nozzles? etc... I am just looking to get a
Electronics Forum | Tue Sep 17 15:47:04 EDT 2013 | 18424
Good day all, I wanted to get a quick poll from the folks running SAC305 in their selective soldering equipment. How are final results? How repeatable is the process, any machine related failures? pumps? nozzles? etc... I am just looking to get a
Electronics Forum | Tue Aug 28 11:12:23 EDT 2007 | grics
This is what I was thinking, but I am being beat up pretty badly by the selective solder. Ambient temperature is anywhere in the the neighborhood of 76 - 80 degrees F. I am not sure of the RH, but I wouldn't think that would be my issue... One of
Electronics Forum | Fri May 23 18:55:20 EDT 2008 | gregoryyork
This is one of the biggest mistakes with the Lead Free process. We have all listened to the 'industry experts' and followed their advice and unfortunately got it wrong. Keep the dwell times (dependant on alloy selection) the same as Leaded so you are
Electronics Forum | Fri Jan 22 15:48:14 EST 1999 | Chrys
| Hello, | | I will be evaluating and qualifying two equipment types. The first is a fountain soldering device. I need practical advice on all the stuff you guys and gals know about as good, bad, ugly, best applications, setup, limitations, and all
Electronics Forum | Mon Nov 09 09:44:22 EST 2015 | davef
Purpose. This describes setting-up a wave soldering system set-up for a new assembly design or checking a wave solder machine operation with a test board. Applicability. To be used for new design printed circuit assembles and during machine accept
Electronics Forum | Sun Nov 08 15:27:25 EST 2015 | davef
Thinner: Flux thinner, NOT paint thinner We kept a spare stone in thinner in inventory. We cut PVC pipe to size, cap in one end, screw thread on the other, stone inside, filled with flux thinner and covered with a screw cap. I don't remember who we
Electronics Forum | Wed Jan 06 04:51:16 EST 1999 | Earl Moon
| | A question for you all! | | | | Back in the good old days, we didn't always know how clean was clean. Much has changed. Much hasn't. | | | | My question concerns cleaning under, through, and around tight spaces. Way back when, we could not clea
Electronics Forum | Tue Oct 12 17:40:01 EDT 1999 | Brian W.
| | | A question for you all! | | | | | | Back in the good old days, we didn't always know how clean was clean. Much has changed. Much hasn't. | | | | | | My question concerns cleaning under, through, and around tight spaces. Way back when, we coul
Electronics Forum | Tue Dec 08 12:44:52 EST 2020 | janwillemreusink
Who is using two sorts of tin in one selective soldering machine with to solder pots? So then the soldering program selects the correct pot (tin). What are the risks? Adding wrong tin in the wrong pot. Mixing up the nozzles?
1 |